一种铁氧体与金属的焊接方法技术
Welding method for ferrite and metal
The invention discloses a method for welding of ferrite and metal, which comprises the following steps: 1), the sintering forming silver silver coated layer on the surface of ferrite; 2), covering the barrier layer on the outer layer of silver; 3), will be placed between the solder and ferrite matrix metal welding prepare welding parts, ferrite and metal. The silver layer is coated by the barrier layer, can not only realize the solid welding of ferrite and metal, and can effectively solve the solder on the silver layer corrosion problems, can improve the welding parts of the working temperature, to ensure the effective bonding area of ferrite and metal, ensure satisfying thermal and mechanical requirements and, to further expand its application in high vacuum field.
【技术实现步骤摘要】
一种铁氧体与金属的焊接方法
本专利技术涉及微波器件的焊接
，具体涉及一种铁氧体与金属的焊接方法。
技术介绍
铁氧体材料由于具有良好的电磁损耗特性和高频特性，其可以有效衰减或吸收射频能量，在抗电磁干扰、大功率微波负载以及荷电粒子加速器等方面具有非常广泛的应用。一般地，从器件整体研制上考虑，需要将铁氧体材料同金属材料进行固定焊接来实现其功能。通常的方式是使用有机粘合剂进行粘接，但有机物的导热系数较低，不能耐高温，而且不适合高真空环境，其使用范围非常有限。另一种方式是通过磁控溅射镀金属膜或者被银的方式将铁氧体进行预先金属化，然后使用焊料将其与金属材料进行焊接。磁控溅射镀膜工艺复杂，生产成本较高，并且难以大批量连续生产以及制备大尺寸的铁氧体器件。被银法工艺简单，不需要昂贵的金属化装置，是一种非常适合于工业化生产的铁氧体与金属焊接的方法。目前被银法主要的工艺过程为先在铁氧体表面烧渗银层，然后直接使用低温焊料将其与金属进行焊接。通常选用的焊料为Ag-Sn合金，其焊接温度较低(300-380℃)，又由于Sn具有较高的饱和蒸气压，使其并不适合于在高温和高真空环境下使用。专利...
【技术保护点】
一种铁氧体与金属的焊接方法，其特征在于，包括以下步骤：1)、在铁氧体表面涂银进行烧渗形成银层；2)、在所述银层外覆盖阻挡层；3)、将焊料置于由步骤2)得到的铁氧体与金属基体之间进行焊接，制得铁氧体与金属基体的焊接部件。
【技术特征摘要】
1.一种铁氧体与金属的焊接方法，其特征在于，包括以下步骤：1)、在铁氧体表面涂银进行烧渗形成银层；2)、在所述银层外覆盖阻挡层；3)、将焊料置于由步骤2)得到的铁氧体与金属基体之间进行焊接，制得铁氧体与金属基体的焊接部件。2.根据权利要求1所述的一种铁氧体与金属的焊接方法，其特征在于，所述阻挡层至少包括镍、钒、铜、镍钒合金、镍铜合金中的一种。3.根据权利要求1所述的一种铁氧体与金属的焊接方法，其特征在于，所述阻挡层的厚度为2～15微米。4.根据权利要求3所述的一种铁氧体与金属的焊接方法，其特征在于，所述阻挡层包括多层，每层的厚度为2～4微米。5.根据权利要求1所述的一种铁氧体与金属的焊接方法，其特征在于，所述金属基体的表面覆盖有过渡金属层。6.根据权利要求5所述的一...
【专利技术属性】
技术研发人员：杨洁，陈欣，陈弹蛋，黄刚，刘平，向军，李天涛，刘尔祥，徐紫阳，陈德彪，龙继东，
申请(专利权)人：中国工程物理研究院流体物理研究所，
类型：发明
国别省市：四川,51