一种丙烯醛液相催化氧化制备丙烯酸的方法技术

本发明专利技术公开了一种丙烯醛液相催化氧化制备丙烯酸的方法。该方法以有机溶剂为反应溶剂体系，加入丙烯醛和掺氮碳纳米管，通入氧气，在压力0.1~2 MPa、温度80～100℃的条件下，搅拌反应0.1~24 h，将丙烯醛氧化为丙烯酸。本发明专利技术方法具有丙烯酸选择性高、反应条件温和、操作简单、成本低、催化剂简单易得、容易回收以及稳定性好等优点，且丙烯醛的转化率达到20%以上，丙烯酸的选择性达到60%以上。

Method for preparing acrylic acid by liquid phase catalytic oxidation of acrolein

The invention discloses a method for preparing acrylic acid by liquid phase catalytic oxidation of acrolein. This method uses organic solvent as a reaction solvent, adding acrolein and nitrogen doped carbon nanotubes, oxygen pressure, MPa, 0.1~2 in temperature 80 to 100 DEG C under the condition of stirring reaction of 0.1~24 h, the oxidation of acrolein to acrylic acid. The method of the invention has the advantages of acrylic high selectivity, mild reaction conditions, simple operation, low cost, easy to get, easy catalyst recovery and good stability, and acrolein conversion reached more than 20%, the selectivity of acrylic acid reached more than 60%.

【技术实现步骤摘要】
一种丙烯醛液相催化氧化制备丙烯酸的方法
本专利技术涉及丙烯酸制备
，具体涉及丙烯醛液相催化氧化制备丙烯酸的方法。
技术介绍
丙烯酸(AA)作为最简单的不饱和一元羧酸，是一种应用广泛的工业原料。丙烯酸在工业上的主要用途是制造附加值高的丙烯酸酯类，它的应用涉及建材、胶黏剂、涂料、高吸水性树脂、皮革、化纤、造纸、助剂、洗涤剂、固化剂及印刷等各行各业；丙烯酸也容易发生均聚或共聚反应，生成聚丙烯酸盐，可用作各种软化剂、食品保鲜剂及增稠剂等常用助剂。自从20世纪60年代末以来，丙烯醛气相催化氧化制备丙烯酸的反应已经受到广泛关注。复合金属氧化物是丙烯酸生产过程中活性较好的催化剂，经过多年的研究实践，含Mo、V的复合金属氧化物被确定为具有较好的丙烯醛氧化活性。目前，大量专利报道主要针对催化剂的活性、选择性和稳定性等方面进行改进。专利CN104437526A在催化剂制备的过程中，先通过钾的可溶性溶液与硅溶胶混合合成了K含量相对稳定的Mo-V系复合氧化物催化剂，280℃时丙烯醛转化率达99.2％，丙烯酸选择性达99.5％，而且3000h后仍旧能够保持良好的稳定性。专利CN104399483A报道了本文档来自技高网...

【技术保护点】
一种丙烯醛液相催化氧化制备丙烯酸的方法，其特征在于，包括如下步骤：以有机溶剂为反应溶剂体系，加入丙烯醛和掺氮碳纳米管，通入氧气，低温加热搅拌下进行反应，反应结束后冷却至室温，过滤，分离液相混合物，得到丙烯酸。

【技术特征摘要】
1.一种丙烯醛液相催化氧化制备丙烯酸的方法，其特征在于，包括如下步骤：以有机溶剂为反应溶剂体系，加入丙烯醛和掺氮碳纳米管，通入氧气，低温加热搅拌下进行反应，反应结束后冷却至室温，过滤，分离液相混合物，得到丙烯酸。2.根据权利要求1所述的一种丙烯醛液相催化氧化制备丙烯酸的方法，其特征在于，所述有机溶剂包括1,2-二氯乙烷、四氯化碳和甲苯中的一种以上。3.根据权利要求1所述的一种丙烯醛液相催化氧化制备丙烯酸的方法，其特征在于，所述掺氮碳纳米管与丙烯醛的质量比为1:45~1:25。4.根据权利要求1所述的一种丙烯醛液相催化氧化制备丙烯酸的方法，其特征在于，所述反应...

【专利技术属性】
技术研发人员：余皓，曹永海，侯萌萌，彭峰，王红娟，
申请(专利权)人：华南理工大学，
类型：发明
国别省市：广东,44