The invention relates to a room temperature curing epoxy resin expansive soil modifier, the epoxy resin expansive soil modifier by the following raw materials were prepared: a) epoxy resin; b) magnetic ionic liquid; and C) of sulfhydryl compounds. The epoxy resin swelling soil improver can also include an aquatic heat type heating agent. The invention also provides a preparation method and an application method of the epoxy resin expansion improver. The invention has the advantages that (1) by in situ curing epoxy resin and curing agent and magnetic ionic liquid ion exchange to expansive soil, permanent and significantly reduce the expansion rate of the expansive soil; and (2) preparation and construction method is simple and suitable for industrial production.
【技术实现步骤摘要】
一种室温固化环氧树脂膨胀土改良剂及其制备和使用方法
本专利技术涉及岩土工程
具体来说，本专利技术涉及一种室温固化环氧树脂膨胀土改良剂，室温固化环氧树脂膨胀土改良剂的制备方法，以及室温固化环氧树脂膨胀土改良剂的使用方法。
技术介绍
膨胀土是一种具有较多裂隙和较大胀缩性质的地质体。膨胀土粘土成分主要由强亲水性矿物蒙脱土与伊利石组成，它们吸水时膨胀，失水时收缩，使得膨胀土发生反复变形。膨胀土的这些性质对工程建筑物等有严重的破坏作用，因此需要改良膨胀土来降低膨胀土的膨胀性。目前，改良膨胀土的方法主要可分为物理改良方法和化学改良方法。化学改良方法能永久改变膨胀土的晶层结构，因此从建筑施工的长期稳定性和安全性而言可能比物理改良方法略胜一筹。化学改良方法之一使用聚合物来改良膨胀土，但其尚存在以下问题：1)聚合物只通过包裹、机械啮合等物理作用来提高粘土颗粒之间的连接作用，因此降低膨胀土膨胀性以及增加膨胀土强度的作用有限；2)聚合物是疏水性的且在聚合过程中不吸收水分，膨胀土颗粒表面存在的吸附水膜会削弱聚合物网络对膨胀土颗粒之间连接的加强作用；以及3)聚合物难以在室温条件下快...
【技术保护点】
一种室温固化环氧树脂膨胀土改良剂，所述环氧树脂膨胀土改良剂通过下述原料组分来制备：a)环氧树脂；b)磁性离子液体；以及c)巯基化合物；其中，b)磁性离子液体的结构如下述结构式(I)所示：
【技术特征摘要】
1.一种室温固化环氧树脂膨胀土改良剂，所述环氧树脂膨胀土改良剂通过下述原料组分来制备：a)环氧树脂；b)磁性离子液体；以及c)巯基化合物；其中，b)磁性离子液体的结构如下述结构式(I)所示：在式(I)中，n＝1-15，X为Cl或Br。2.如权利要求1所述的环氧树脂膨胀土改良剂，其特征在于，还包括遇水生热型发热剂。3.如权利要求1或2所述的环氧树脂膨胀土改良剂，其特征在于，还包括消泡剂、流平剂、防沉剂、粘度调节剂和稀释剂中的一种或多种。4.如权利要求1或2所述的环氧树脂膨胀土改良剂，其特征在于，所述环氧树脂包括缩水甘油酯类环氧树脂，所述甘油酯类环氧树脂包括下述中的一种或多种：四氢邻苯二甲酸二缩水甘油酯，邻苯二甲酸二缩水甘油酯，间苯二甲酸二缩水甘油酯或六氢邻苯二甲酸二缩水甘油酯。5.如权利要求1或2所述的环氧树脂膨胀土改良剂，其特征在于，所述巯基化合物包括下述中的一种或多种：聚硫醇、液态聚硫橡...