A new type of metal welding method, which comprises a first metal plate and the second metal plate, the first metal plate and the second metal plate after docking, the stirring head pressure on the docking at the joint between the first metal plate and the second metal plate, and the stirring head to rotate at high speed and walking along the joint of the first metal plate and the second metal plate, the stirring head walking the first metal plate, second metal plates on the path of plastic deformation, the plastic deformation of the first metal plate, second metal plate part of the stirring mixing head under the mixed with each other to form a welding. The invention uses joint mixing head of metal plate pressure, and through the high-speed stirring, makes the metal plastic deformation after mixing together so as to achieve the effect of welding, the weld quality is high, can achieve zero defect.
【技术实现步骤摘要】
金属新型焊接方法
本专利技术涉及一种金属焊接方法。
技术介绍
金属件之间的传统焊接方法包括熔焊、钎焊等方法，这些焊接方法起焊缝处的难以达到零缺陷的效果，因此迫切需要一种焊缝质量更好的金属焊接方法。
技术实现思路
为了克服现有金属焊接方法的上述不足，本专利技术提供一种焊缝质量更好的金属新型焊接方法。本专利技术解决其技术问题的技术方案是：一种金属新型焊接方法，包括第一金属板和第二金属板，将第一金属板和第二金属板对接后，在第一金属板和第二金属板的对接处采用搅拌头对该对接处施加压力，同时所述的搅拌头高速旋转并沿着第一金属板和第二金属板的对接处行走，使得搅拌头行走路径上的第一金属板、第二金属板产生塑性变形，塑性变形部分的第一金属板、第二金属板在搅拌头的搅拌作用下相互混合从而形成焊接。进一步，所述的第一金属板、第二金属板为相同材质。进一步，所述的第一金属板、第二金属板均为铜板或铜合金板。或者：所述的第一金属板、第二金属板为不同的材质。进一步，设定期望温度，对焊接处的工件的温度进行测量，并根据测得的温度与期望温度的比较调整搅拌头的下压程度和/或搅拌头的旋转速度和/或搅拌头的行走速度...
【技术保护点】
一种金属新型焊接方法，包括第一金属板和第二金属板，其特征在于：将第一金属板和第二金属板对接后，在第一金属板和第二金属板的对接处采用搅拌头对该对接处施加压力，同时所述的搅拌头高速旋转并沿着第一金属板和第二金属板的对接处行走，使得搅拌头行走路径上的第一金属板、第二金属板产生塑性变形，塑性变形部分的第一金属板、第二金属板在搅拌头的搅拌作用下相互混合从而形成焊接。
【技术特征摘要】
1.一种金属新型焊接方法，包括第一金属板和第二金属板，其特征在于：将第一金属板和第二金属板对接后，在第一金属板和第二金属板的对接处采用搅拌头对该对接处施加压力，同时所述的搅拌头高速旋转并沿着第一金属板和第二金属板的对接处行走，使得搅拌头行走路径上的第一金属板、第二金属板产生塑性变形，塑性变形部分的第一金属板、第二金属板在搅拌头的搅拌作用下相互混合从而形成焊接。2.如权利要求1所述的金属新型焊接方法，其特征在于：所述的第一金属板、第二金属板为相同材质。3.如权利要求1所述的金属新型焊接方法，其...
【专利技术属性】
技术研发人员：章德均，刁海波，
申请(专利权)人：宁波金凤焊割机械制造有限公司，
类型：发明
国别省市：浙江,33