本发明专利技术涉及一种制备玻璃‑陶瓷体的方法，其包括步骤：提供基础玻璃体和对该基础玻璃体进行热处理，由此形成嵌在玻璃基质中的结晶相。根据本发明专利技术，该基础玻璃体是由包含以下组分的组合物制成的：基于该组合物总重量，65‑72wt%的SiO2，至少10.1wt%的Li2O和至少10.1wt%的Al2O3，Li2O与Al2O3的比例为1：1‑1.5：1。该热处理包括成核步骤，随后是在不同温度的几个结晶步骤，由此形成至少两个不同的结晶相。

Preparation method of glass ceramics

The invention relates to a preparation method of glass ceramic body, comprises the steps of: providing basis of vitreous body and heat treatment of the foundation formed in crystal vitreous body, embedded in the glass matrix. According to the invention, the base is made of vitreous body composition comprising the following components: the total weight of the composition based on SiO2 65 72wt%, at least 10.1wt% Li2O and at least 10.1wt% Al2O3, Li2O and Al2O3 ratio of 1:1 1.5:1. The heat treatment comprises a nucleation step, followed by several crystallization steps at different temperatures, whereby at least two different crystalline phases are formed.

【技术实现步骤摘要】
制备玻璃-陶瓷体的方法本申请是申请号为201280019087.6（PCT/EP2012/001709）、申请日为2012年4月20日的专利技术专利申请的分案申请。
本专利技术涉及一种制备玻璃-陶瓷体的方法，用于所述方法的玻璃组合物，可通过所述方法获得的玻璃-陶瓷体以及所述玻璃-陶瓷体用于牙齿修复物的用途。
技术介绍
玻璃-陶瓷材料包含无定形(玻璃)相和嵌在该无定形相中的一个或多个结晶(陶瓷)相。由于无定形和结晶相的同时存在，玻璃-陶瓷具有玻璃和陶瓷二者的许多性能。它们被用于许多不同的
，例如作为炉灶面、炊具和烘焙用具，作为用于磁盘的基片或作为用于数字投影仪的高性能反射器。玻璃-陶瓷在修复牙科学领域是特别令人感兴趣的，在该领域表达了对在功能性和外观方面将表现得恰如它们的天然对应物一样的假体的需要。惯例上，牙齿修复物根据“烤瓷熔附金属”(PFM)方法来制备，其中将载体金属框架与构成了假体颜色的陶瓷材料镶面层结合使用。根据这种方法制备修复物意味着诸多的制造步骤，因此是费力的。PFM方法已经通过用非金属无机框架替代金属框架而获得了进一步的发展。就这一点而言，已经提出了填充有氧化铝颗粒本文档来自技高网...

【技术保护点】
玻璃组合物，基于组合物的总重量其包含65‑72wt%的SiO2，至少10.1wt%的Li2O和至少10.1wt%的Al2O3， Li2O与Al2O3的比例为1:1‑1.5:1。

【技术特征摘要】
2011.04.20 EP 11003315.61.玻璃组合物，基于组合物的总重量其包含65-72wt%的SiO2，至少10.1wt%的Li2O和至少10.1wt%的Al2O3，Li2O与Al2O3的比例为1:1-1.5:1。2.根据权利要求1的玻璃组合物，其包含最多15wt%的Li2O和/或最多15wt%的Al2O3。3.根据权利要求1-2任一项的玻璃组合物，基于组合物的总重量其进一步包含0-2wt%的K2O，1-4wt%的Na2O，0-1.5wt%的CaO，0-1.0wt%的MgO，0-1.5wt%的B2O3，0-1.5wt%的CeO2，1-5wt%的P2O5，0-3wt%的CaF2，0-2.0wt%的AlF3，0-1.0wt%的...

【专利技术属性】
技术研发人员：M博祖奇拉茨卡，K乔勒瓦科瓦斯卡，K拉茨卡，
申请(专利权)人：斯特劳曼控股公司，
类型：发明
国别省市：瑞士,CH