聚乙二醇修饰的磁性微球在制备肿瘤近红外光热试剂中的应用制造技术

本发明专利技术属于生物材料技术领域，具体为聚乙二醇修饰的磁性微球在制备肿瘤近红外光热试剂中的应用。PEG修饰的磁性微球，其在近红外光区具有较强的吸收，并且可以将吸收的近红外光能转换成热量，使得肿瘤部位局部温度升高将肿瘤细胞杀死，可用于制备近红外光热治疗的光热试剂。同现有光热试剂相比，磁性微球生物相容性好、可降解，尺寸易于调控，磁饱和强度较高，广泛用于生物医学领域，因此具有极高的临床应用价值。

Application of polyethylene glycol modified magnetic microspheres in preparation of near infrared photothermal reagents for tumor

The invention belongs to the technical field of biological materials, in particular to the application of polyethylene glycol modified magnetic microspheres in the preparation of a near infrared photothermal agent for tumor. PEG modified magnetic microspheres, has strong absorption in the near infrared region, near infrared light absorption and can be converted into heat, the temperature will increase local tumor site to kill tumor cells, can be used for thermal reagent preparation of near infrared photothermal therapy. Compared with the photo thermal reagents, magnetic microspheres have good biocompatibility, biodegradability, size, ease of regulation and high magnetic saturation. They are widely used in the field of biomedicine, so they have very high clinical value.

【技术实现步骤摘要】
聚乙二醇修饰的磁性微球在制备肿瘤近红外光热试剂中的应用
本专利技术属于生物材料
，具体涉及聚乙二醇(PEG)修饰的磁性微球在制备近红外光热转换试剂中的应用，用于肿瘤的近红外光热治疗。
技术介绍
癌症正成为危害人类生命健康的最大威胁。目前治疗癌症的方式主要有手术治疗、化疗、放射性治疗，但是手术治疗很难去除体内所有的癌细胞，化疗具有有毒副作用，且容易诱发癌细胞的耐药性，放射性治疗容易破坏人体的免疫系统。而光热治疗是一种新兴的用于治疗癌症的高选择性和微创技术，通过光热试剂在局部近红外的激光照射，将近红外的能量转变为热能，从而可以有效的杀伤肿瘤细胞。近年来，人们研究较多的光热试剂主要有金属基材料、碳基材料、硫化铜等无机纳米材料和以近红外染料、以聚合物等为代表的有机纳米材料。尽管这些材料已经在荷瘤小鼠体内取得了比较好的效果，然而这些材料由于成本高、制备过程复杂以及需要进行大量的表面修饰，妨碍了它们进一步的临床转化。因此，开发一种成本低廉、简单高效并且生物相容性良好的新型光热试剂对于未来的临床肿瘤光热治疗具有重大的意义。磁性氧化铁粒子由于其良好的生物安全性，尺寸易调控，易分离，磁饱和强度高本文档来自技高网...

【技术保护点】
聚乙二醇修饰的磁性微球在制备肿瘤近红外光热试剂中的应用，光热试剂中PEG修饰的磁性微球的浓度为50~500 μg/mL。

【技术特征摘要】
1.聚乙二醇修饰的磁性微球在制备肿瘤近红外光热试剂中的应用，光热试剂中PEG修饰的磁性微球的浓度为50~500μg/mL。2.根据权利要求1所述的应用，其特征在于，所述的PEG修饰的磁性微球主要成分为Fe3O4纳米粒子，其粒径范围在100~600nm...

【专利技术属性】
技术研发人员：杨武利，彭海豹，曹勇斌，
申请(专利权)人：复旦大学，
类型：发明
国别省市：上海,31