The invention discloses an epoxy powder coating, the raw material components according to the mass ratio: 70, 60 epoxy resin curing agent 3, 5 isocyanuric acid three glycidyl ester 1 3, dispersant 0.5 1 copies, 30 copies, 20 titanium dioxide leveling agent 0.5 1, 0.5 gliant powder 1.5, talcum powder 5 10 copies, 5 copies, 2 Barium Sulfate Pigment 3 1. The invention of epoxy resin, filler, curing agent, dispersing agent, leveling agent, flow agent, pigment by high-speed mixing, melt extrusion, pressure roller pressing, crushing, sieving and filtering, made of powder coating; with no solvent, no pollution, energy saving and environmental protection, reduce the labor intensity and has the advantages of high mechanical strength and coating. The production cost is low, can effectively reduce the production cost of enterprises.
【技术实现步骤摘要】
一种环氧粉末涂料及其制备方法
本专利技术涉及涂料生产
，具体涉及一种环氧粉末涂料及其制备方法。
技术介绍
电磁线是用以制造电工产品中的线圈或绕组的绝缘电线，电磁线必须满足多种使用和制造工艺上的要求，包括其形状、规格、能短时和长期在高温下工作，以及承受某些场合中的强烈振动和高速下的离心力，高电压下的耐受电晕和击穿，特殊气氛下的耐化学腐蚀等。然而目前机电行业常用的无机类氧化膜绝缘铝线的生产过程中还使用大量浓硫酸，在生产过程中有大量挥发有刺激性气体，不仅对操作人员有伤害，而且对生产车间和周围环境带来严重的腐蚀和污染。
技术实现思路
本专利技术为了克服无机类氧化膜绝缘铝线生产过程中使用大量浓硫酸的缺陷问题，提供一种环氧粉末涂料及其制备方法，将环氧树脂、填料、固化剂、分散剂、流平剂、流动助剂、颜料经高速混合、熔融挤出、压辊压片、粉碎、筛分过滤，制成粉末涂料。为实现上述目的，本专利技术采用的技术方案是：一种环氧粉末涂料，各原料组分按质量份比为：环氧树脂60-70份、固化剂3-5份、异氰尿酸三缩水甘油酯1-3份、分散剂0.5-1份、钛白粉20-30份、流平剂0.5-1份、粉末...
【技术保护点】
一种环氧粉末涂料，其特征在于，各原料组分按质量份比为：环氧树脂60‑70份、固化剂3‑5份、异氰尿酸三缩水甘油酯1‑3份、分散剂0.5‑1份、钛白粉20‑30份、流平剂0.5‑1份、粉末流动助剂0.5‑1.5份、滑石粉5‑10份、硫酸钡2‑5份、颜料1‑3份。
【技术特征摘要】
1.一种环氧粉末涂料，其特征在于，各原料组分按质量份比为：环氧树脂60-70份、固化剂3-5份、异氰尿酸三缩水甘油酯1-3份、分散剂0.5-1份、钛白粉20-30份、流平剂0.5-1份、粉末流动助剂0.5-1.5份、滑石粉5-10份、硫酸钡2-5份、颜料1-3份。2.如权利要求1所述的一种环氧粉末涂料，其特征在于，各原料组分按质量份比为：环氧树脂65份、固化剂4份、异氰尿酸三缩水甘油酯2份、分散剂0.75份、钛白粉25份、流平剂0.75份、粉末流动助剂1份、滑石粉8份、硫酸钡3份、颜料2份。3.如权利要求1所述的一种环氧粉末涂料，其特征在于：所述环氧树脂为双酚A型环氧树脂或酚醛改性环氧树脂。4.如权利要求1所述的一种环氧粉末涂料，其特征在于：所述粉末流动助剂为经过电荷改性的低分子量聚乙烯，聚乙烯的粒径为8...
【专利技术属性】
技术研发人员：鲍熊，
申请(专利权)人：安徽联硕实业有限公司，
类型：发明
国别省市：安徽,34