The present invention provides an epoxy paint, which comprises the following raw materials in parts by weight: 55 fluid epoxy resin, melamine formaldehyde resin 32, styrene butadiene thermoplastic elastomer 9, acrylonitrile butadiene styrene copolymer 3 copies, 36 copies of pigments, corrosion inhibitor 3, polyamide polyamine aqueous solution 50 a water 45, the mass fraction of the polyamide polyamine aqueous solution was 45%, the corrosion inhibitor for organic zinc salt, the anti rust pigment for multi zinc borate. The invention has the advantages that the crosslinking density is greatly improved, the gloss of the paint film is improved, the acid and alkali resistance are greatly improved, and the flexibility is good.
【技术实现步骤摘要】
一种环氧漆
本专利技术涉及涂料,具体涉及一种环氧漆。
技术介绍
目前环氧漆的耐蚀水性漆的硬度、和耐腐蚀性均不够,不能满足恶劣环境下耐蚀水性漆的要求。
技术实现思路
本专利技术的目的是提供一种环氧漆,解决现有技术中的一个或多个问题。根据本专利技术的一个方面,提供一种环氧漆,包括以下重量份数的原料:流体环氧树脂55份,三聚氰胺甲醛树脂32份,苯乙烯-丁二烯热塑性弹性体9份,丙烯腈-丁二烯-苯乙烯共聚物3份,颜料36份,腐蚀抑制剂3份,聚酰胺-聚胺水溶液50份,水45份,聚酰胺-聚胺水溶液的质量分数为45%,腐蚀抑制剂为有机锌盐,防锈颜料为多向硼酸锌。本专利技术有效大大提高交联密度,提高漆膜光泽,耐酸耐碱性都大大提高,柔韧性好。具体实施方式本专利技术提供一种环氧漆,包括以下重量份数的原料:流体环氧树脂55份,三聚氰胺甲醛树脂32份,苯乙烯-丁二烯热塑性弹性体9份,丙烯腈-丁二烯-苯乙烯共聚物3份,颜料36份,腐蚀抑制剂3份,聚酰胺-聚胺水溶液50份,水45份,聚酰胺-聚胺水溶液的质量分数为45%,腐蚀抑制剂为有机锌盐,防锈颜料为多向硼酸锌。本专利技术有效大大提高交联密度,提高漆膜光泽,耐酸耐碱性都大大提高,柔韧性好。以上表述仅为本专利技术的优选方式,应当指出,对本领域的普通技术人员来说,在不脱离本专利技术创造构思的前提下,还可以做出若干变形和改进,这些也应视为本专利技术的保护范围之内。
【技术保护点】
一种环氧漆,其特征在于,包括以下重量份数的原料:流体环氧树脂55份,三聚氰胺甲醛树脂32份,苯乙烯‑丁二烯热塑性弹性体9份,丙烯腈‑丁二烯‑苯乙烯共聚物3份,颜料36份,腐蚀抑制剂3份,聚酰胺‑聚胺水溶液50份,水45份,所述聚酰胺‑聚胺水溶液的质量分数为45%,所述腐蚀抑制剂为有机锌盐,所述防锈颜料为多向硼酸锌。
【技术特征摘要】
1.一种环氧漆,其特征在于,包括以下重量份数的原料:流体环氧树脂55份,三聚氰胺甲醛树脂32份,苯乙烯-丁二烯热塑性弹性体9份,丙烯腈-丁二烯-苯乙烯共聚物3份...