The invention provides a waterproof leather fatliquoring agent, including the weight of raw materials as follows: isopropanol 315 copies, 240 copies of acrylonitrile, vinyl stearate 215, methacrylic acid 55, sixteen ene two azo isobutyronitrile 15 copies, 5 copies, 7 copies of the mercaptan; isopropanol is heated to 82 C the stearic acid vinyl acetate, acrylonitrile, methyl acrylate, styrene, cyclohexene, sixteen two azo isobutyronitrile, mercaptan 1 hours after cooling by NaOH and to PH for 6. The invention has the advantages of light color, high degree of saturation, good light resistance, no yellowing phenomenon, forming a solid complex with chromium in leather fiber, and is a permanent leather waterproof fatliquoring agent. The leather is soft, elastic, light resistant and wet washed after adding ester.
【技术实现步骤摘要】
一种皮革防水加脂剂
本专利技术涉及加脂剂的原料配比，具体涉及一种皮革防水加脂剂。
技术介绍
目前的皮革加脂剂由于原料的配比不佳，不能形成良好的防水膜，防水性能受到影响。
技术实现思路
本专利技术的目的是提供一种皮革防水加脂剂，解决现有技术中的一个或多个问题。根据本专利技术的一个方面，提供一种皮革防水加脂剂，包括重量份数如下的原料：异丙醇315份，丙烯腈240份、硬脂酸乙烯酯215份，甲基丙烯酸55份，十六烯15份，偶氮二异丁腈5份，硫醇7份；将所述异丙醇加热至82℃时加入硬脂酸乙烯酯、丙烯腈、甲基丙烯酸、苯乙烯、十六烯、偶氮二异丁腈、硫醇反应1小时，冷却后用NaOH中和至PH为6。本专利技术提供的一种皮革防水加脂剂，色泽浅、饱和度高、耐光性好，无泛黄现象，可与皮革纤维中的铬形成牢固的络合物，是永久性皮革防水加脂剂。加酯后成革柔软，弹性好，耐光，耐湿洗。具体实施方法本专利技术提供一种皮革防水加脂剂，包括重量份数如下的原料：异丙醇315份，丙烯腈240份、硬脂酸乙烯酯215份，甲基丙烯酸55份，十六烯15份，偶氮二异丁腈5份，硫醇7份；将所述异丙醇加热至82℃时加入硬脂酸...
【技术保护点】
一种皮革防水加脂剂，其特征在于，包括重量分数如下的原料：异丙醇315份，丙烯腈240份、硬脂酸乙烯酯215份，甲基丙烯酸55份，十六烯15份，偶氮二异丁腈5份，硫醇7份；将所述异丙醇加热至82℃时加入硬脂酸乙烯酯、丙烯腈、甲基丙烯酸、苯乙烯、十六烯、偶氮二异丁腈、硫醇反应1小时，冷却后用NaOH中和至PH为6。
【技术特征摘要】
1.一种皮革防水加脂剂，其特征在于，包括重量分数如下的原料：异丙醇315份，丙烯腈240份、硬脂酸乙烯酯215份，甲基丙烯酸55份，十六烯15份，偶氮二异丁腈...