The invention discloses a structure containing sulfite polymer fatliquoring agent and a preparation method thereof, including the following steps: Poly glycerol and maleic anhydride was prepared by esterification of carboxyl containing reactive intermediates A, A intermediate and long chain fatty alcohol further esterified to obtain the intermediate B, intermediate B and sulfites sulfitation the reaction is a sulfite containing structure of polymer fatliquor. The synthesis process of the structure containing the sulfite containing Polymer Fatliquor is simple and environment-friendly, and the organic solvent is not used, and the synthesis process has no toxic and harmful substances. The structural grease containing the sulfite polymer has good fatliquoring effect, filling performance, electrolyte stability resistance and organic solvent extraction performance, and simultaneously reduces the COD content of the fatliquoring waste liquor.
【技术实现步骤摘要】
一种含亚硫酸盐结构的聚合物加脂剂及其制备方法
本专利技术属于皮革化学品制备领域，具体涉及一种含亚硫酸盐结构的聚合物加脂剂及其制备方法
技术介绍
加脂剂是制革过程中使用量最大的化学品之一。传统的加脂剂主要是小分子的天然动植物油脂改性产物，其功能是润滑皮纤维，赋予皮革柔软舒适的手感。聚合物加脂剂是一种多功能皮革化学品，分子结构中同时具有可以润滑皮革纤维的长链烷烃和含羧基等亲水基团的低分子量聚合物，这种结构使其具有润滑纤维作用的同时又具备填充功能。与低分子量加脂剂相比，聚合物加脂剂具有以下特点：(1)使复鞣和加脂功能合二为一，减少操作工序；(2)结合力强、在皮革中不易迁移、加脂效果持久，适用于汽车坐垫革、耐水洗革等高档革的生产；(3)经金属盐封闭后，可提高皮胶原纤维的疏水性，可应用于防水革的加脂；(4)一定程度上减少复鞣剂和加脂剂的总用量，使皮革手感轻盈，卫生性能得到最大程度保持；(5)吸收率高，能有效降低制革废水中的BOD和COD值。总之，由于聚合物加脂剂具有较高技术含量和工业应用价值，近年来聚合物加脂剂的制备及性能研究受到广泛的重视。聚合物加脂剂的制备路线根据长链烷...
【技术保护点】
一种含亚硫酸盐结构的聚合物加脂剂，其特征在于其分子式为：
【技术特征摘要】
1.一种含亚硫酸盐结构的聚合物加脂剂，其特征在于其分子式为：其中：R：为C8-18的长链烷烃；n:3～20。2.一种含亚硫酸盐结构的聚合物加脂剂的制备方法，其特征在于包括以下步骤：(1)将聚甘油和马来酸酐置于反应器中，在80～100℃条件下进行酯化反应3～6h，得到中间体A，所述聚甘油分子上的羟基和马来酸酐的摩尔比为1：1.05～1.1；(2)向中间体A中加入长链脂肪醇，通氮气，于150～200℃条件下进行酯化反应，反应时间3～6h,得到中间体B，所述长链脂肪醇与步骤(1)中马来酸酐的摩尔比为1：1；(3)将中间体B降温至60-70℃，加入亚硫酸盐水溶液，升温至80～90度反应3～5...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。