The invention relates to a preparation method of aqueous epoxy colloid, which belongs to the field of coating and chemical engineering. The raw materials include: epoxy resin 20~30 wt%, 20~30 wt epoxy diluent%, two ethanol amine 5~10 wt%, wt%, 1~5 acetic acid deionized water% wt 30~40. The aqueous colloid preparation steps are as follows: first epoxy resin and active diluent to uniform and transparent, and then control the temperature of 80~85 DEG C adding two ethanol, isothermal reaction 1~1.5h, adding acetic acid neutralization, be transparent and uniform water epoxy colloid under stirring adding deionized water. Compared with the traditional chemical modification method, the invention has simple operation, low reaction temperature and short time and almost no VOCs emission. The size of colloidal particles reaches nanometer scale, good stability, good hydrophilicity and low viscosity.
【技术实现步骤摘要】
一种水性环氧树脂胶体及其制备方法
本专利技术涉及一种水性环氧树脂胶体及其制备方法，属涂料化工领域。
技术介绍
环氧树脂是指含有环氧基团(EpoxyGroup,EPG)的高分子聚合物，但有些分子量不大、含有两个或两个以上环氧基团的化合物，由于它能在固化剂作用下聚合成塑料，因此人们习惯上也把这类环氧化合物称为环氧树脂。环氧树脂类涂料广泛应用生活中方方面面，在涂料中占有至关重要的地位。环氧树脂与基体间的附着力好，因其含有羟基和醚键，所以对湿面也有较好的结合力；环氧树脂固化剂种类多，固化体积收缩仅有2%，固化后能形成三维网状结构，具有较好的耐水性、耐酸碱性、耐油性。环氧树脂种类繁多，目前常用的环氧树脂有E-51、E-44、E-20等。环氧树脂不溶于水，目前常用的环氧树脂水性化方法有：机械法、化学改性法、外加乳化剂法等。机械法即直接乳化法，可用球磨机、胶体磨等将固体环氧树脂预先磨成微米级的环氧树脂粉末，然后加入乳化剂水溶液，再通过机械搅拌将粒子分散于水中。机械法制备水性环氧树脂乳液的优点是工艺简单，所需乳化剂用量较少，但乳液中环氧树脂微粒尺寸大、形状不规则，所配得的乳液稳定...
【技术保护点】
一种水性环氧树脂胶体及其制备方法，其特征在于：所述水性环氧树脂胶体呈均一透明状态，其成分及质量比如下：环氧树脂20~30 wt%、环氧稀释剂AGE 15~25 wt %、改性剂二乙醇胺5~10 wt %、中和剂乙酸1~5 wt %、去离子水30~40 wt %。
【技术特征摘要】
1.一种水性环氧树脂胶体及其制备方法，其特征在于：所述水性环氧树脂胶体呈均一透明状态，其成分及质量比如下：环氧树脂20~30wt%、环氧稀释剂AGE15~25wt%、改性剂二乙醇胺5~10wt%、中和剂乙酸1~5wt%、去离子水30~40wt%。2.如权利要求1所述水性环氧树脂胶体，其特征在于制备方法包括以下步骤：（1）改性：将环氧树脂...
【专利技术属性】
技术研发人员：刘海萍，张松，毕四富，左银成，王春雨，曹立新，
申请(专利权)人：哈尔滨工业大学威海，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。