The invention discloses a preparation method of poly (lactic acid) (PLA) nucleating agent based on bamboo powder. It includes the following steps: first, at room temperature, the bamboo fiber into 200 preliminary 325, the diameter of 45 around 75 micron powder; after sodium hydroxide solution treatment, after drying the bamboo powder again ground into superfine powder 0.01 20 micron, the weak acid treatment in a high-speed mixer after the product is polylactic acid A efficient nucleating agent. The present invention in the polylactic acid content is 0.1 5%, can significantly improve the crystallization rate, increase the crystallinity of the products, improve the heat resistance of products. In the process of injection molding, mould crystallization process is not needed, the molding cycle of the product is shortened, and the production efficiency is improved.
【技术实现步骤摘要】
一种基于竹粉的聚乳酸成核剂的制备方法
本专利技术属于材料工程
，特别涉及一种聚乳酸（PLA）成核剂的制备方法。
技术介绍
聚乳酸（PLA）材料是一种完全可生物降解的环境友好的高分子材料，具有强度高、流动性好、易于成型的特点，在一次性用品、包装材料等领域具有广阔的应用前景。但是PLA材料耐热性能差，只能在55℃以下使用。为了提高它的耐热性能，扩大其应用领域，研究者进行了大量的研究工作，取得了一定的成绩，主要是采用加入成核剂提高结晶度，改善其耐热性能。但到目前为止，对于PLA材料具有高效成核作用的非常少。由于PLA材料的结晶速率小，结晶度低，即使加入了成核剂，其注射成型制品仍然需要经过模内结晶过程，且结晶温度在100-120℃，制品才能达到耐热性能要求，而这种模内结晶技术工艺，成型周期长，生产效率低，且能源消耗大，使得生产制品的成本高。因此，需要有一种高效的PLA成核剂，在成型过程中，使得PLA制品具有高的结晶度，从而改善制品的耐热性能。基于竹粉的PLA成核剂的突出特点是：由于竹粉具有可降解性，保证了PLA材料体系具有完全可降解性。
技术实现思路
为了解决PLA材料...
【技术保护点】
一种基于竹粉的聚乳酸成核剂的制备方法，其特征在于，包括以下步骤：（1）在室温下，把竹纤维初步磨成粉末；（2）将步骤（1）所得竹粉放入氢氧化钠溶液中，缓慢搅拌1~9小时，然后离心除水，并进行干燥；（3）把干燥后的竹粉再次磨细；（4）把再次磨细后的竹粉放入高速混合机，采用弱酸在50~150℃改性处理2~15min，然后干燥得到聚乳酸成核剂。
【技术特征摘要】
1.一种基于竹粉的聚乳酸成核剂的制备方法，其特征在于，包括以下步骤：（1）在室温下，把竹纤维初步磨成粉末；（2）将步骤（1）所得竹粉放入氢氧化钠溶液中，缓慢搅拌1~9小时，然后离心除水，并进行干燥；（3）把干燥后的竹粉再次磨细；（4）把再次磨细后的竹粉放入高速混合机，采用弱酸在50~150℃改性处理2~15min，然后干燥得到聚乳酸成核剂。2.如权利要求1所述的聚乳酸成核剂的制备方法，其特征在于：步骤（1）中的粉末，颗粒尺寸控制在200~325目，粒径在45~75微米。3.如权利要求1所述的聚乳酸成核剂的制备方法，其特征在于：步骤（2）中，干燥...
【专利技术属性】
技术研发人员：戴文利，莫兰，彭显达，陈枝晴，
申请(专利权)人：湘潭大学，
类型：发明
国别省市：湖南,43