The invention discloses a preparation method of a polypropylene organic composite nucleating agent, which is composed of a Sorbitol Nucleating Agent and 1,3,5- benzene three formic acid () (BTCA-TCHA), and the proportion is 7:3~3:7. The invention uses Sorbitol Nucleating Agent and 1,3,5- benzene three formic acid three (cyclohexylamine) nucleation, has a great improvement on the crystallization behavior and mechanical properties of polypropylene and transparency, and because of the synergy between the two, reduce the two kinds of nucleating agent effective usage. The two kinds of nucleating agents were dissolved in N, N-, and methyl formamide in a proportion of, and then mixed with 3~5min at high speed. The invention has simple operation process and can be used for industrial production.
【技术实现步骤摘要】
本专利技术涉及一种聚丙烯成核剂的制备方法,具体涉及一种有机复合成核剂的制备方法,属于复合材料领域。
技术介绍
聚丙烯作为五大通用塑料中发展最快的品种,具有原料来源丰富、价格较低、易于加工成型、产品性能优良等优点,故而具有非常广泛的用途。但聚丙烯也存在一些不足之处(抗冲击性差、高温刚性不足、透明性差等),为了扩大聚丙烯的应用领域,延长其使用寿命,就必须对聚丙烯进行改性。现有对聚丙烯改性效果最好的是成核剂改性,添加成核剂可以改变聚丙烯的结晶特性,从而影响其物理机械性能。二亚苄基山梨醇类成核剂是目前应用最广泛的成核剂,其中1,3:2,4-二亚苄基山梨醇(DBS)、1,3:2,4-二(对甲基亚苄基)山梨醇(MDBS)、1,3:2,4-二(3,4-二甲基亚苄基)山梨醇(DMDBS)分别为第一、二、三代山梨醇类成核剂,这类成核剂成核效果好,对聚丙烯透明性能改善尤为明显,但是MDBS、DMDBS熔点一般较高,会影响其在聚丙烯中的分散性,且成本较高。成核剂1,3,5-苯三甲酸三(环己胺)对聚丙烯热性能和力学性能有着明显的提高,尤其对刚性的改善突出,但是对聚丙烯透明性的改善不如山梨醇类成核剂。将1,3,5-苯三甲酸三(环己胺)与山梨醇类成核剂按照比例配成复合成核剂,可以减少二者的有效使用量,使成本降低,对聚丙烯的力学性能和透明性有着更大的提高,且操作工艺简单,可用于工业化生产。
技术实现思路
本专利技术提供了一种聚丙烯用有机复合成核剂的制备方法,该成核剂由山梨醇类成核剂与1,3,5-苯三甲酸三(环己胺)(BTCA-TCH ...
【技术保护点】
一种聚丙烯有机复合成核剂的制备方法,其特征在于,所述复合成核剂由山梨醇类成核剂与1,3,5‑苯三甲酸三( 环己胺) ( BTCA‑TCHA)组成,该复合成核剂由以下步骤合成:取山梨醇类成核剂和 1,3,5‑苯三甲酸三(环己胺) (BTCA‑TCHA),按照一定的重量比溶于入N,N‑二甲基甲酰胺(DMF),在高速搅拌下搅拌3~5min,即得到目标成核剂。
【技术特征摘要】
1.一种聚丙烯有机复合成核剂的制备方法,其特征在于,所述复合成核剂由山梨醇类成核剂与1,3,5-苯三甲酸三(环己胺)(BTCA-TCHA)组成,该复合成核剂由以下步骤合成:取山梨醇类成核剂和1,3,5-苯三甲酸三(环己胺)(BTCA-TCHA),按照一定的重量比溶于入N,N-二甲基甲酰胺(DMF),在高速搅拌下搅拌3~5min,即得到目标成核剂。
2.根据权利要求1所述的一种聚丙烯有机复合成...
【专利技术属性】
技术研发人员:张跃飞,刘抱,何彬,侯焕焕,李丹,
申请(专利权)人:长沙理工大学,
类型:发明
国别省市:湖南;43