The invention provides a preparation method of ceramics, according to the weight of a material, except modified polycarboxylate superplasticizer and mixing of raw materials made of clay, then add the right amount of water, the clay dispersed into suspension with concentration of 15 40%, 2 hours, 1 dry milling after adding modified poly carboxylic acid water reducing agent, adding water, preparation of ceramic glaze; conventional preparation process; blank forming, color glaze, high temperature burning, cooling and forming, can. The formula of the invention of the ceramic clay rich, low cost, compared with the existing ceramic clay, enhance the plasticity of ceramic clay, thus increasing the calcination temperature of the ceramic yield.
【技术实现步骤摘要】
一种陶瓷的制备方法
本专利技术涉及陶瓷领域，确切地说是一种陶瓷的制备方法。
技术介绍
在陶瓷生产中使用陶瓷分散剂（减水剂），既可使得陶瓷泥浆具有好的流动性，又能降低其含水率，改善陶瓷的性能，具有提高产品性能和节能减排的作用。陶瓷减水剂（又称分散剂）作为陶瓷添加剂的一种，主要功能是破坏陶瓷料浆粒子的絮凝结构，使料浆在水分含量较低的情况下依然具有较好的分散性和较低的粘度。在陶瓷生产过程中起到节能降耗的作用。陶瓷减水剂可广泛用于陶瓷工业的造泥、磨浆、制釉等陶瓷生产工艺过程。在陶瓷生产中使用性能优异的减水剂能降低陶瓷的生产成本，提高产品质量，使陶瓷生产工业朝向效益高、质量好和能耗低的方向发展。
技术实现思路
本专利技术的目的在于提供一种解决再生混凝土制品强度要求的问题的陶瓷的制备方法。上述目的通过以下方案实现：一种陶瓷的制备方法，其特征在于：包括以下步骤：（1）按照如下重量份取料：废白瓷粉10-15、石英粉30-45、长石粉7-12、氧化铝4-7、硅藻土30-55、高岭土10-25、硬脂酸0.1-0.2、改性聚羧酸减水剂1-2；（2）将上述组分除改性聚羧酸减水剂外原料混合制成...
【技术保护点】
一种陶瓷的制备方法，其特征在于：包括以下步骤：（1）按照如下重量份取料：废白瓷粉10‑15、石英粉30‑45、长石粉7‑12、氧化铝4‑7、硅藻土30‑55、高岭土10‑25、硬脂酸0.1‑0.2、改性聚羧酸减水剂1‑2；（2）将上述组分除改性聚羧酸减水剂外原料混合制成瓷土后，再加入适量水，将瓷土分散成浓度15‑40％的分散悬浮液，球磨1‑2小时，干燥后，再加入改性聚羧酸减水剂，加适量水，配制成陶瓷坯料；（3）常规工艺配制釉料；（4）坯料成型后，施釉上色、高温烧制、冷却成型，即可。
【技术特征摘要】
1.一种陶瓷的制备方法，其特征在于：包括以下步骤：（1）按照如下重量份取料：废白瓷粉10-15、石英粉30-45、长石粉7-12、氧化铝4-7、硅藻土30-55、高岭土10-25、硬脂酸0.1-0.2、改性聚羧酸减水剂1-2；（2）将上述组分除改性聚羧酸减水剂外原料混合制成瓷土后，再加入适量水，将瓷土分散成浓度15-40％的分散悬浮液，球磨1-2小时，干燥后，再加入改性聚羧酸减水剂，加适量水，配制成陶瓷坯料；（3）常规工艺配制釉料；（4）坯料成型后，施釉上色、高温烧制、冷却成型，即可。2.根据权利要求1所述的陶瓷的制备方法，其特征在于：改性聚羧酸减水剂的制备方法为：造纸废料白泥放于调浆桶中，调成含固量为10-30％的浆料；将浆料加热至40-50℃，再与玉米秸秆混匀，再加入十二烷基硫酸钠，搅拌50-80min后，干燥，挤压成块，得到块状物料备用；于反应釜中注...
【专利技术属性】
技术研发人员：张媛媛，
申请(专利权)人：安徽省宿州市贯华化工有限公司，
类型：发明
国别省市：安徽,34