一种三元碳化物纳米带的制备方法技术
Preparation method of three element carbide nano band
The invention discloses a preparation method of three element carbide nanobelts, which belongs to the field of nanometer materials. The method of the invention is as follows: the response of a certain amount of MAX phase material with alkali solution, and then after separation, washing and drying to obtain the three yuan carbide nanoribbons; the method of the invention has the advantages of simple method, low requirement on equipment condition, without expensive instruments, and green environmental protection. The prepared three yuan carbide nano belt has a unique structure and excellent electrical conductivity, good mechanical properties, high surface chemical reactivity and good self lubrication performance and friction performance, can be effectively applied in the field of energy storage and friction field, has great practical value.
【技术实现步骤摘要】
一种三元碳化物纳米带的制备方法
本专利技术涉及一种三元碳化物纳米带的制备方法，属于纳米材料领域。
技术介绍
近年来一种被称为MAX相的材料兼具了金属和陶瓷的优良性能。具有良好的导热导电性、可塑性、电化学性能、自润滑性、耐磨性能，因此MAX相材料可被广泛应用于储能领域及摩擦领域。但是应用于储能器件时，大尺寸的块状MAX相材料具有诸多不便，同时作为增强剂或添加剂应用于摩擦领域时大尺寸的MAX相材料的结合性能与摩擦性能相对较低，因此制备纳米级的MAX相材料尤为重要。目前制备纳米级MAX相材料的方法主要为球磨-超声剥离法，但是该制备方法过程繁琐，能耗高，周期时间长，对设备要求较高，所以设计开发一种新的纳米尺度的MAX相材料的制备方法具有重要意义。
技术实现思路
本专利技术的技术目的即是针对上述技术现状，提供一种制备流程简单、绿色环保、对设备要求不高且省时、高效的纳米级材料的制备方法，利用该制备方法能够得到形貌优良、具有纳米带状结构的MAX相材料。本专利技术的技术方案可通过以下步骤实现：将MAX相材料与碱溶液混合均匀，然后将混合物料置于保护气氛下反应完成后分离、洗涤、干燥得到三...
【技术保护点】
一种三元碳化物纳米带的制备方法，其特征在于：将MAX相材料与碱溶液混合均匀，然后将混合物料置于保护气氛下进行反应，反应完成后经分离、洗涤、干燥得到三元碳化物纳米带。
【技术特征摘要】
1.一种三元碳化物纳米带的制备方法，其特征在于：将MAX相材料与碱溶液混合均匀，然后将混合物料置于保护气氛下进行反应，反应完成后经分离、洗涤、干燥得到三元碳化物纳米带。2.根据权利要求1所述三元碳化物纳米带的制备方法，其特征在于：所述MAX相中M为过渡金属元素Ti、Zr、Hf、V、Ta、Cr、Sc、Mo中的一种或多种，A为Al、Ga、Ge、As、Cd、In、Sn、Ti、Pb中的一种或多种，X为C。3.根据权利要求1所述三元碳化物纳米带的制备方法，其特征在于：所述碱溶液为氢氧化钾溶液、氢氧化锂溶液、氢氧化钠溶液、氨水溶液中的一种或两种及以上按任意比例混合得到的混合溶液。4.根据权利要求1或2所述三元碳化物纳米带的制备方法，其特征在于：...