一种新颖微纳米普鲁士蓝颗粒的制备方法技术
Preparation method of novel micro nano Prussian blue particle
The invention relates to a preparation method of novel micro nano Prussian blue particles, in particular to a two precursor solution of potassium ferricyanide and ferric chloride mixture of Prussian blue in the appropriate conditions of pH and stirring to synthesize nano Prussian blue particles. The synthetic device adopted by the invention is simple, uses common beaker as a reaction vessel and a magnetic stirrer with stirring function. The synthesis of Prussian blue particles by controlling the conversion rate of Prussian blue in solution resulted in the synthesis of Prussian blue particles. The micro nano materials can be used in solid state batteries, electrochromic devices, molecular magnets and other fields of application.
【技术实现步骤摘要】
一种新颖微纳米普鲁士蓝颗粒的制备方法
本专利技术涉及一种新颖微纳米普鲁士蓝颗粒的制备方法，具体涉及一种以普鲁士蓝的两种前驱液为反应物，通过调控溶液为适当的pH值后，采用机械搅拌方法合成出微纳米级别的普鲁士蓝颗粒，属于材料合成化学领域。
技术介绍
普鲁士蓝及其类似物是一类多核过渡金属铁氰化物，具有和沸石相似的开放结构。由于在H2O2和O2还原过程表现出优异的催化活性和选择性，被认为是一种人工过氧化氢酶，并且广泛应用于生物传感器的构建方面。此外，由于其快速的电荷转移和磁性变化特性，在分子磁体器件、电致变色显示器、能量储存和电池领域也具有潜在的应用前景。通常合成普鲁士蓝颗粒的方法是将Fe3+和[Fe(CN)6]4-两种前驱液充分混合后即可，但由于该方法反应速率较快，很难控制普鲁士蓝颗粒的大小和形貌，而这些特性非常影响普鲁士蓝的性质。因此探索出反应可控的普鲁士蓝纳米颗粒合成新工艺成为当前研究的热点。
技术实现思路
本专利技术提出了一种新颖微纳米普鲁士蓝颗粒的新合成技术。利用该技术制备的微纳米普鲁士蓝颗粒可用作H2O2分子电催化反应的电子媒介体，在分子磁体器件和固体电池、电致变色器件领域也具有潜在的应用价值。为了实现上述目的，本专利技术采用了以下的技术方案：本专利技术涉及一种新颖微纳米普鲁士蓝颗粒合成的新技术，具体涉及一种以FeCl3和K3[Fe(CN)6]作为合成普鲁士蓝微纳米颗粒的前驱液，通过调控溶液的pH值，在不断的机械搅拌条件下可制备出大小均匀的微纳米普鲁士蓝颗粒。本专利技术所述的制备方法以FeCl3和K3[Fe(CN)6]溶液作为前驱液。本专利技术所述的制备方...
【技术保护点】
一种新颖微纳米普鲁士蓝颗粒的制备方法，其特征在于：将普鲁士蓝的两种前驱液三氯化铁和铁氰化钾溶液混合后，调节溶液的pH为适当值，在室温下不断连续搅拌，经一段反应时间即可制备出微纳米普鲁士蓝颗粒。
【技术特征摘要】
1.一种新颖微纳米普鲁士蓝颗粒的制备方法，其特征在于：将普鲁士蓝的两种前驱液三氯化铁和铁氰化钾溶液混合后，调节溶液的pH为适当值，在室温下不断连续搅拌，经一段反应时间即可制备出微纳米普鲁士蓝颗粒。2.根据权利要求1所述的一种微纳米普鲁士...
【专利技术属性】
技术研发人员：陈体伟，余小娜，陈怡萌，
申请(专利权)人：许昌学院，
类型：发明
国别省市：河南,41