The invention provides a method for the synthesis of aromatic Guanguan non-woven cloth adhesive. The invention adopts the following technical scheme: using two kinds of polyol, toluene diisocyanate, six methylene diisocyanate monomer, and adding poly silane coupling agent by pre polymerization, neutralization and emulsification, preparation of polymer chain extender. The silicon oxygen bond structure of polyurethane adhesive prepared by the method of can significantly improve the thermal stability and mechanical properties of polyurethane adhesive layer, and improve the water resistance, weather resistance, acid and alkali resistance and high temperature performance.
【技术实现步骤摘要】
一种用于芳纶无纬布的胶黏剂的制备方法
本专利技术涉及一种胶黏剂的制备方法,特别是一种用于芳纶芳纶无纬布的胶黏剂的制备方法。
技术介绍
材料的防弹作用主要表现在两个方面:一方面是将弹体碎裂后形成的破片弹开;另一方面是通过防弹材料消释弹头的动能。机织物材料的交织点多,受弹击后,子弹的动能可通过交织点上纱线的相互作用得以传递,从而使子弹或弹片的冲击力能在较大区域内吸收。但与此同时,交织点在无形中又起了固定端的作用。在固定末端所形成的反射波与原来的入射波会产生同向叠加,使纱线受到的拉伸作用大大增强,在超过其断裂强度后断裂,从而对材料的防弹性能产生不利影响。要获取最好的抗冲击性能最好是采用单向的、没有交织点的材料。芳纶无纬布正是根据此理论,采用芳纶纤维单向平行排列并用热理性树脂粘结,再经0。/90。正交复合层压而成。粘合剂是生产芳纶无纬布必不可少的原料,而且对芳纶无纬布的性能有至关重要的作用。热塑性聚氨酯是一类性能优良的弹性体树脂,近些年来随着原料和合成工艺的改进,水性聚氨酯的综合性能得到显著提高。与溶剂型胶粘剂体系相比,水性聚氨酯以水为溶剂,胶液的含固量和粘度随时间变化不明显,有利于无纬布预浸成型工艺控制。此外,水性聚氨酯施胶过程中毒性挥发物少。对工作人员危害程度较小,具有突出的环保性。
技术实现思路
本专利技术提供一种用于芳纶纶无纬布的胶黏剂的合成方法,在聚氨酯的预聚合过程中加入聚硅烷偶联剂,有机硅分子中既含有机基团,又含无机硅原子,具有比较低的表面能,它在胶膜干燥过程中向表面富集,使其具有良好的乳液稳定性,此外结构中硅氧键的引入可以显著的提高聚氨酯胶层的热稳定性和 ...
【技术保护点】
一种用于芳纶无纬布的胶黏剂的制备方法,其特征为:将聚己二酸‑1,4‑丁二醇酯二醇‑A组分145‑150份、聚己二酸‑1,4‑丁二醇酯二醇‑B组分120‑125份加入烧瓶,均匀搅拌,加入甲苯二异氰酸酯61‑63份,六亚甲基二异氰酸酯21‑23份,加入苯基三(三甲基硅氧烷基)硅烷7‑8份,加热至85度,保持3h;降温至70度,加入2,2‑二羟甲基丙酸11‑13份、N‑甲基吡咯烷酮71‑73份继续搅拌4h;降温至60度,加入三乙胺13‑15份,搅拌0.5h。
【技术特征摘要】
1.一种用于芳纶无纬布的胶黏剂的制备方法,其特征为:将聚己二酸-1,4-丁二醇酯二醇-A组分145-150份、聚己二酸-1,4-丁二醇酯二醇-B组分120-125份加入烧瓶,均匀搅拌,加入甲苯二异氰酸酯61-63份,六亚甲基二异氰酸酯21-23份,加入苯基三(三甲基硅氧烷基)硅烷7-8份,加热至85度,保持3h;降温至70度,加入2,2-二羟甲基丙酸11-13份、N-甲基吡咯烷酮71-73份继续搅拌4...
【专利技术属性】
技术研发人员:杨洛阳,杨永,
申请(专利权)人:上海飞顿新材料科技有限公司,
类型:发明
国别省市:上海,31