The invention relates to a polyvinylidene fluoride hydrophobic separation membrane and a preparation method thereof, which belongs to the technical field of hydrophobic separation membrane. Include the following in accordance with the weight of raw materials: polyvinylidene fluoride 20, N 15, N two DMF 75 85 copies, 5 copies, 3 butanol butyl acetate 3 5, three 3 5 butyl phosphate, polyethylene glycol PEG 1000 10, 5 anhydrous lithium chloride 3 5 sodium chloride, 3 5 copies, 500 copies, 300 deionized water 5 alcohol 10, isopropanol 5 10 copies, 5 copies of the 2 hydrophobic coating solution. The polyvinylidene fluoride hydrophobic separation membrane of the present invention is hydrophobic and can resist pollution.
【技术实现步骤摘要】
本专利技术涉及一种分离膜及其制备方法，更具体地说，本专利技术涉及一种聚偏氟乙烯疏水分离膜及其制备方法，属于疏水分离膜
技术介绍
近几十年来，高分子膜广泛应用在各种气体、液体分离领域，如微滤、超滤、反渗透和纳滤，而聚偏氟乙烯(PVDF)膜以其优异的综合性能成为应用最广泛的高分子膜之一。聚偏氟乙烯(PVDF)具有良好的热稳定性、化学稳定性和机械强度。聚偏氟乙烯(PVDF)膜主要的制备方法为相转化法。在相转化制备过程中，聚(PVDF)膜的结构及性能受铸膜液组成的影响，而添加剂是其主要因素之一。在铸膜液中添加适合的添加剂是制备适当结构和渗透性能膜最简便和最有效的方法。不同添加剂的种类、含量及分子量的不同对聚砜膜结构影响较大。而通过对其表面进行疏水化处理可以显著提高其疏水性。目前，PVDF亲水微孔膜已成功地应用于化工、纺织、食品、生化等工业领域。PVDF疏水微孔膜在膜蒸馏等领域显示出广阔的应用前景，但由于PVDF材料本身疏水性能的限制，使其在膜分离的应用中仍然存在膜亲水渗透、不耐污染等问题。因此对PVDF膜进行超疏水改性以提高其疏水性能和抗污染性成为人们研究的主...
【技术保护点】
一种聚偏氟乙烯疏水分离膜，其特征在于：包括以下按照重量份数计的原料：聚偏氟乙烯 15‑20份N，N－二甲基甲酰胺 75‑85份正丁醇 3‑5份醋酸丁酯 3‑5份磷酸三丁酯 3‑5份聚乙二醇PEG‑1000 5‑10份无水氯化锂 ...
【技术特征摘要】
1.一种聚偏氟乙烯疏水分离膜，其特征在于：包括以下按照重量份数计的原料：聚偏氟乙烯15-20份N，N－二甲基甲酰胺75-85份正丁醇3-5份醋酸丁酯3-5份磷酸三丁酯3-5份聚乙二醇PEG-10005-10份无水氯化锂3-5份氯化钠3-5份去离子水300-500份酒精5-10份异丙醇5-10份疏水涂覆液2-5份。2.根据权利要求1所述的一种聚偏氟乙烯疏水分离膜的制备方法，其特征在于：包括以下工艺步骤：A、按配方要求精确称取聚偏氟乙烯于盛有预先称量好的N，N－二甲基甲酰胺磨口瓶内，让其充分溶胀1-2h；溶胀后于65℃热水浴中震荡溶解3-4h；B、逐渐加入正丁醇、醋酸丁酯、磷酸三丁...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。