The invention discloses a method for preparing a superhydrophobic copper surface with a plant leaf structure. In the method of super hydrophobic plant leaves as template preparation, first by sintering a non oxidizing atmosphere, get the carbon template with leaf structure, and then through the electroplating method in the carbon template surface plating a thin layer of copper, copper surface has a leaf blade structure, the copper surface fluorine silane modified low surface energy materials after having super hydrophobic properties. The microstructure of copper surface prepared by the invention can be a good legacy of plant leaves, high degree of natural, and the electroplating method in the film leaves the surface of the template. The copper plating grain increase surface roughness of copper surface structure, which has super hydrophobic properties.
【技术实现步骤摘要】
本专利技术属于材料制备
，涉及一种制备具有植物叶片结构超疏水铜表面的方法，具体涉及一种利用电镀制备具有植物叶片结构超疏水铜表面的方法。
技术介绍
铜及其合金是人类应用最早和最广的一种有色金属，其导电和导热性好，但在制冷、低温运行和户外使用的铜制零部件中，铜由于表面能较高，水分子易吸附聚集，极易结冰，严重影响了铜产品的导热和导电性能，给产品和设备的稳定工作带来了较大的危害。传统的防覆冰方法大多基于除冰、融冰思路，如热力融冰、过电流融冰、短路融冰、带负荷融冰、高频脉冲电流加热振荡、敷设发热导体等，但这些方法不能从根本上解决问题。将铜做成超疏水材料可以有效地解决这些问题，超疏水的铜表面能有效的降低水的附着以及结冰，并且表面自清洁能力强，使得实际铜的使用寿命及使用效率得到大幅提升。目前，超疏水铜表面主要是通过人工的方法构造粗糙结构，比如湿化学刻蚀法、氧化法、电沉积法和浸泡法等方法，然后用具有低表面能的物质进行表面修饰制得超疏水材料。弯艳玲等人采用高速电火花线切割机床在铜表面构筑复合粗糙结构，经自组装技术处理后得到了超疏水铜表面，制得的超疏水铜材料接触角达到了153...
【技术保护点】
一种制备具有植物叶片结构超疏水铜表面的方法，其特征在于，具体步骤如下：步骤1，将干燥的超疏水性植物叶片置于非氧化性气氛中烧结，烧结温度大于600℃，升温速率不大于5℃/min，制得具有植物叶片结构的碳素模板；步骤2，将碳素模板作为阴极，在0.1～0.7mol/L硫酸铜溶液中电镀1～5min，电流密度为0.02～0.04A/cm2，至碳素模板表面附着一层铜层为止；步骤3，将表面镀铜的碳素模板浸泡在氟硅烷的体积分数为10％～20％的异丙醇和氟硅烷的混合溶液中，浸泡结束后取出干燥，得到具有植物叶片结构超疏水铜表面。
【技术特征摘要】
1.一种制备具有植物叶片结构超疏水铜表面的方法，其特征在于，具体步骤如下：步骤1，将干燥的超疏水性植物叶片置于非氧化性气氛中烧结，烧结温度大于600℃，升温速率不大于5℃/min，制得具有植物叶片结构的碳素模板；步骤2，将碳素模板作为阴极，在0.1～0.7mol/L硫酸铜溶液中电镀1～5min，电流密度为0.02～0.04A/cm2，至碳素模板表面附着一层铜层为止；步骤3，将表面镀铜的碳素模板浸泡在氟硅烷的体积分数为10％～20％的异...
【专利技术属性】
技术研发人员：王天驰，陈凯，孔见，赵一卓，周哲，刘子恒，
申请(专利权)人：南京理工大学，
类型：发明
国别省市：江苏;32