A method of low temperature preparation of lithium niobate ultra-fine powder first, according to the chemical formula LiNbO: 3 Nb: 2 O: 5 and LiCO: 3 powder mixture, then add 50% - 200% mixed powder quality in the mixed powder of salt are mixed uniformly to obtain mixture; secondly, the mixture into a container, at 600 to 800 DEG C. for 5 minutes and 2 hours of calcination; finally, the calcined product grinding, cleaning, filtering to remove salt from cobalt ferrite ultrafine powder. The powder prepared by the invention has the advantages of good grain development degree, fine particle size, sub micron size, small particle size distribution, good crystalline state and light agglomeration. At the same time, the introduction of salt can reduce the synthetic temperature, and has short heat preservation time, low energy consumption, simple process and equipment, convenient operation, cheap and easy raw material, low preparation cost and convenient industrial production. Moreover, the fused salt medium can be reused by simple recrystallization.
【技术实现步骤摘要】
本专利技术属于材料科学领域，具体涉及一种低温制备铌酸锂超细粉体的 方法。
技术介绍
铌酸锂(LiNb03)是一种非常重要的铁电材料，具有很好的铁电、压电、 热释电、介电、电光、声光、光折变和非线性光学效应。.由于LiNb03具有 居里温度高，自发极化强度大,机电耦合系数大且机械品质因数高，声学传 输损耗低等突出的优点，被广泛应用于声表面波器件、高频高温换能器、 光调制器、延迟线及光波导等领域。LiNb03粉体可以用于制备LiNb03陶瓷 和LiNbOa单晶。目前国内外制备"iNb03粉体的方法有固相法、水热法、聚 合物前驱体法，低温燃烧法。固相法合成LiNb03粉体的温度高，通常需要 达到120(TC左右，由于温度很高，容易导致杂相的形成和锂离子的挥发， 実法得到理想化，量比的粉体，而且粉体的粒径较粗。.吁霁等以恥205和 LiOH化0为原料，采用水热法，在26(TC保温24小时，合成了LiNb03粉体。由于NbA是不溶于水和一般的酸碱等溶剂， 所以用水热法需要控制较ift的温.度和压力，并且保温时间非常长，否则难 以成相。赵九蓬等以NbA， LiC03， HF...
【技术保护点】
一种低温制备铌酸锂超细粉体的方法，其特征在于：１）首先，按化学通式ＬｉＮｂＯ↓［３］将Ｎｂ↓［２］Ｏ↓［５］和ＬｉＣＯ↓［３］粉体混合，然后在混合粉体中加入混合粉体质量的５０％－２００％的盐混合均匀得到混合物；２）其次，将混 合物放入容器中，在６００℃－８００℃煅烧５分钟－２小时；３）最后，将煅烧产物研细，清洗，过滤除去盐得到钴铁氧体超细粉体。
【技术特征摘要】
【专利技术属性】
技术研发人员：杨海波，林营，王芬，朱建锋，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：87[中国|西安]