一种含稀土催化剂的聚苯颗粒保温隔热浆料制造技术

一种含稀土催化剂的聚苯颗粒保温隔热浆料，其特征在于，其组成按重量份包括：普通硅酸盐水泥２８０－３２５份；粉煤灰４００－４６０份；熟石灰１３０－１７０份；石膏粉１７－２３份；甲基纤维素２－５份，稀土催化剂２－４份；聚丙烯纤维２－５；聚乙烯醇１７－２５份；膨胀聚苯乙烯５０－６０份；水７０－１００份。本发明专利技术采用的技术方案不但具有良好的保温性能、防水性能，还具有相当的强度，可直接粘贴瓷砖，具有粘贴牢固，并且具有施工简便，综合造价低，利用回收的泡沫塑料资源重复利用，有利于保护环境等优点。

Polyphenyl particle insulation and heat insulation slurry containing rare earth catalyst

A rare earth catalyst containing polystyrene particles insulation slurry, which is characterized in that the composition by weight including: Portland cement 280325 400460; fly ash; lime 130170; gypsum powder 1723; methyl cellulose 2-5, 2 rare earth catalyst; polypropylene fiber 2; polyvinyl alcohol 17-25; expanded polystyrene a continuous water 70-100 50-60. The technical scheme of the invention not only has the heat insulation performance, good waterproof performance, but also has considerable strength, can be directly pasted tiles, with solid paste, and has simple construction, low cost, recycling plastic recycling, to protect the environment etc..

【技术实现步骤摘要】

本专利技术属于建筑保温材料
，特别是涉及到一种含稀土催化剂的聚 苯颗粒保温隔热浆料.
技术介绍
随着建筑材料改革的发展，代替粘土砖的各种新型墙体材料相继问世，但 是各种空心砌块的保温性能较差，还需在表面制作保温层，市场上的保温材料 也种类繁多，如以硅酸盐为主体的保温材料。这些材料大都用于内墙或管路、 设备等保温涂覆，外墙保温材料由于要求防水性能和强度比较高， 一般的保温 材料尚不能满足需要。现在流行的外墙保温材料大都不能直接与瓷砖粘贴，还 需要制作铁丝网辅助固定层和石膏或水泥罩面。
技术实现思路
本专利技术的目的在于提供一种含稀土催化剂的聚苯颗粒保温隔热浆料，用在 外墙的外表面直接制作外保温层。本专利技术的目的通过以下技术方案实现。一种含稀土催化剂的聚苯颗粒保温隔热浆料，其组成按重量份，包括普 通硅酸盐水泥2 8 0 - 3 2 5份；粉煤灰4 0 0 - 4 6 0份；熟石灰l 3 0 -1 7 0份；石膏粉l 7 - 2 3份；曱基纤维素2 - 5份，稀土催化剂2 - 4份； 聚丙烯纤维2 - 5 ;聚乙烯醇1 7 - 2 5份；膨胀聚苯乙烯50-60份；水 70—100份。本文档来自技高网...

【技术保护点】
一种含稀土催化剂的聚苯颗粒保温隔热浆料，其特征在于：其组成按重量份，包括：普通硅酸盐水泥２８０－３２５份；粉煤灰４００－４６０份；熟石灰１３０－１７０份；石膏粉１７－２３份；甲基纤维素２－５份，稀土催化剂２－４份；聚丙烯纤维２－５；聚乙烯醇１７－２５份；膨胀聚苯乙烯５０－６０份；水７０－１００份。