The invention discloses a solid phase synthesis of ceramic powder material combustion method, generally speaking, this method is that the insoluble salt precursor mixed with organic matter, after drying, combustion required ceramic powder materials in oxygen atmosphere. According to the stoichiometric ratio and insoluble salt precursor, organic compounds and metal ions by Molby in the 1.5 - 3 range: 1 weigh organic compounds, insoluble salt precursor mixed with organic matter, after drying, the ratio of oxygen and air for 0.2 to 1: 1 oxygen atmosphere burning to ceramic powder materials. The solid phase combustion method for synthesizing the ceramic powder material has the advantages of low production cost, energy saving, no environmental pollution, and is suitable for large-scale industrial production.
【技术实现步骤摘要】
本专利技术属于陶瓷粉体材料制备工艺领域，特别是涉及一种合成陶瓷粉体材料的固相燃 烧法、该法合成的陶瓷粉体材料和利用该材料制备的陶瓷。
技术介绍
与金属、塑料相比，陶瓷材料具有优异的耐高温、抗腐蚀、耐磨损性及良好的电气性 能等，广泛地应用于尖端科技邻域，如空间技术、海洋技术和生物工程领域等(苏毅黄 云祥，云南化工1997.2， 13)。而陶瓷制作工艺中的一个基本特点就是以粉体为原料，经 成型和烧结，形成多晶烧结体。陶瓷粉体的质量直接影响最终成品的质量，因此发展陶瓷 的首要问题是要有符合要求的原料——粉体。现代高科技陶瓷材料对粉体的基本要求是高 纯、超细、组分均匀、团聚程度小。为了提高陶瓷粉体的物理和化学特性，很多种陶瓷粉 体合成技术随之发展起来。目前，国际上有多种陶瓷粉体的制备方法，大致可分为两类粉碎法和合成法(陆辟 疆，李春燕，精细化工工艺，北京化学工业出版社，1996， 403)。粉碎法主要采用各种 机械粉碎方法，固相合成中的物理粉碎法就是其中的一种，即采用细磨设备，使用大且硬 的介质，利用介质和物料间的相互研磨和冲击，来研磨比它小得多的晶粒尺寸的粉料 (Pa...
【技术保护点】
一种合成陶瓷粉体材料的固相燃烧法，其特征在于，将不溶性盐前驱体与有机物均匀混合，经过干燥后，在氧气氛下燃烧得到所需陶瓷粉体材料。
【技术特征摘要】
【专利技术属性】
技术研发人员：徐志军，初瑞清，
申请(专利权)人：聊城大学，
类型：发明
国别省市：37[中国|山东]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。