The invention discloses a heat stabilized low radiation composite membrane glass and a production process thereof. The present invention is on a glass substrate covered with a composite film composed of bottom dielectric layer, a first protective layer, a layer of silver, second protective layer and the surface of the dielectric layer, wherein the bottom dielectric layer is aluminum nitride, the thickness of 40 to 55nm; the two protective layer for stainless steel, nickel chromium alloy or their part of the oxides or nitrides, the thickness of 1 to 10nm; the silver layer thickness of 10 ~ 18NM; the surface of the dielectric layer is aluminum nitride or aluminum oxide, the thickness is 40 ~ 65nm. The heat stable low radiation composite membrane glass of the invention can be widely applied to the industries of energy saving, building glass, automobile glass, etc., and can reduce the heat loss of the glass and reduce the energy consumption of the heating in winter and the air conditioner in summer.
【技术实现步骤摘要】
本专利技术涉及一种玻璃，具体地说是一种热稳定低辐射复合膜玻璃，以及生产该玻璃的生产工艺。
技术介绍
玻璃被广泛应用于商用和民用建筑上用来采光。单层玻璃的传热系数通常比建筑物墙壁高得多，门窗的玻璃成为建筑物采暖和空调系统的重要耗能因素。因此，20世纪80年代以来，研究人员开发了低辐射膜中空玻璃，以降低玻璃窗的热损失，减少冬天采暖和夏天空调的能耗。建筑用低辐射膜大体有两种类型，一类为掺杂氧化物半导体低辐射膜，又称透明导电氧化物膜，例如采用在玻璃生产线上高温热分解制备氟掺杂氧化锡低辐射膜，这种低辐射膜具有导电性、金属性和红外反射性，其红外热辐射比较大，约0.20。这种低辐射膜玻璃的主要优点是在空气中稳定性很好，可以长期存放，并且，其在高温下热稳定性也较好，在空气中350℃加热一小时，其膜层不会受到破坏，进一步升温，其红外热辐射比逐步增加，光学性能也逐渐变差。另一类是银基低辐射复合膜，采用真空中磁控溅射技术在玻璃上沉积复合膜，其基本膜层结构为C1/Ag/C2/玻璃，其中金属银层Ag为红外反射层，C1和C2为电介质层。这类低辐射膜需要折射率较高的电介质层，电介质层主要采...
【技术保护点】
热稳定低辐射复合膜玻璃，在玻璃基片上沉积有由底层电介质层、保护层、银层和表层电介质层组成的复合膜，其特征在于，所述底层电介质层为氮化铝，厚度为４０～５５ｎｍ；所述保护层为不锈钢、镍铬合金或它们的部分氧化物或部分氮化物，厚度为１～１０ｎｍ；所述银层的厚度为１０～１８ｎｍ；所述表层电介质层为氮化铝或氧化铝，厚度为４０～６５ｎｍ。
【技术特征摘要】
【专利技术属性】
技术研发人员：章其初，王双，陈革，池华敬，
申请(专利权)人：山东温屏节能玻璃有限公司，
类型：发明
国别省市：37[]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。