The present invention off powder aerogel composite material, composed of aerogel fiber composite mat with flexible coating, coating is adhered on the flexible aerogel fiber composite mat, flexible coating thickness of 0.01mm 0.5mm, and the thermal conductivity of coating on flexible aerogel fiber composite mat increased less than or equal to 10%. Don't drop powder aerogel composite materials and production process of the invention, compared with the currently used on surface of glass fiber cloth, aluminum foil cloth and other methods, low cost, high efficiency, simple process, a good solution to the surface of the aerogel composites easily out of flour, and is favorable for promotion and Application of aerogel fiber products.
【技术实现步骤摘要】
一种不掉粉气凝胶复合材料及其生产工艺
本专利技术属于气凝胶的
，具体是涉及一种不掉粉气凝胶复合材料及其生产工艺。
技术介绍
气凝胶是一种固体物质形态，世界上密度最小的固体，密度可低至3kg每立方米。一般常见的气凝胶为硅气凝胶，其最早由美国科学工作者在1931年制得。气凝胶的种类很多，有硅系，碳系，硫系，金属氧化物系，金属系等等。气凝胶的结构特征是拥有高通透性的圆筒形多分枝纳米多孔三位网络结构，拥有极高孔洞率、极低的密度、高比表面积、超高孔体积率、超低导热系数。由于气凝胶的结构特点，使得气凝胶存在脆性大、柔性差等缺点，大大的限制了气凝胶的应用。虽然目前很多生产厂家以玻璃纤维棉艺或预氧化纤维毡为基体，通过复合二氧化硅凝胶制得复合二氧化硅气凝胶柔性保温毡，但是在使用过程中不可避免的存在气凝胶毡掉落气凝胶粉的情况，掉粉情况不仅给施工带来了不便，给施工人员健康带来了威胁，同时也会降低气凝胶毡本身的性能。目前通常防掉粉方案是采用玻纤布、铝箔布等贴敷在气凝胶纤维毡表面，这种方式人工成本高，不利于大规模生产，并且正反面贴敷后材料的柔性降低，不好卷曲、弯折，储运、施工安装不够...
【技术保护点】
一种不掉粉气凝胶复合材料，其特征在于：由气凝胶纤维复合毡与柔性涂层构成，所述的柔性涂层附着在气凝胶纤维复合毡上，所述柔性涂层的厚度为0.01mm‑0.5mm，且柔性涂层对气凝胶纤维复合毡的导热系数提高≤10%。
【技术特征摘要】
1.一种不掉粉气凝胶复合材料，其特征在于：由气凝胶纤维复合毡与柔性涂层构成，所述的柔性涂层附着在气凝胶纤维复合毡上，所述柔性涂层的厚度为0.01mm-0.5mm，且柔性涂层对气凝胶纤维复合毡的导热系数提高≤10%。2.如权利要求1所述的不掉粉气凝胶复合材料，其特征在于：所述的气凝胶纤维复合毡包括增强纤维和气凝胶，所述的柔性涂层由添加剂和对气凝胶结构不发生破坏成膜物组成。3.如权利要求2所述的不掉粉气凝胶复合材料，其特征在于：所述的增强纤维为玻璃纤维、硅酸铝纤维、莫来石纤维、玄武岩纤维、聚酯纤维、聚丙烯腈纤维、碳纤维或黏胶纤维中的一种或多种混合物，所述的气凝胶为二氧化硅、三氧化二铝、氧化锆、氧化钛、氧化铁、氧化锌、氧化镁、氧化锶或氧化钇中的一种或多种混合物。4.如权利要求2所述的不掉粉气凝胶复合材料，其特征在于：所述的成膜物为改性环氧树脂、聚氨酯、甘油醇酸树脂、三聚氰胺甲醛树脂、...
【专利技术属性】
技术研发人员：姜法兴，熊风，林芬，沈立青，徐君，周水林，赵科仁，姚献东，