本发明专利技术公开了一种改进的玻璃镀膜的方法。在现有镀膜工艺基础上引入了火焰燃烧技术，促使气态镀膜原料或从喷枪喷出的雾化的镀膜溶液，首先进入火焰燃烧的高温区域，然后经过雾化、蒸发、热解、结晶、聚集等步骤，而在热的玻璃板表面沉积形成一层致密、牢固的膜层。本发明专利技术扩大了原材料的选择范围，实现了镀膜产品种类和颜色的多样性；完全摆脱了还原气氛或者惰性气氛对镀膜过程的影响，既能够生产金属氧化物膜层，也能够生产金属膜层；膜层嵌入玻璃板表层，与玻璃板结合为一个整体，解决了膜层耐久性不够的问题。

Improved method for coating glass

The invention discloses an improved method for coating glass. On the basis of existing coating process into the flame combustion technology, the raw materials of gaseous coating or from plating solution spray lance, first enter high-temperature combustion flame region, then after atomization, evaporation, pyrolysis, crystallization and aggregation steps, coating a layer of compact and solid formed on the surface of the glass sheet and the heat deposition. The present invention broaden the scope of selection of raw materials, realize the diversity of coating product types and colors; completely out of reducing atmosphere or inert atmosphere of the coating process, both the production of metal oxide films, but also to the production of metal film; film embedded glass plate surface, combined with the glass plate as a whole, solve the film durability is insufficient.

【技术实现步骤摘要】

【技术保护点】
一种改进的玻璃镀膜的方法，包括以下步骤：（１）将粉末状或液状金属化合物溶解或分散到溶剂中而形成镀膜溶液；（２）镀膜溶液在载体气体的带动下从喷枪喷出形成雾化状态的镀膜溶液；其特征在于，它还包括以下两个步骤：（３）将雾化状态的镀膜溶液进入一火焰燃烧装置的出口处因火焰燃烧所形成的高温区域，并依次经过雾化、蒸发、热解、结晶、聚集之后；（４）在热的玻璃板表面沉积形成牢固且致密的金属氧化物膜层，或者是金属膜层。

【技术特征摘要】

【专利技术属性】
技术研发人员：尚贵才，周杰，赵福志，刘鸿雁，范丽香，
申请(专利权)人：福耀集团双辽有限公司，
类型：发明
国别省市：22[中国|吉林]