纳米油性ATO隔热浆料与制备方法及其应用技术

本发明专利技术公开了纳米油性ＡＴＯ隔热浆料与制备方法及其应用。以重量份数计，该浆料由６７～９０份醇类溶剂，１０～３０份纳米ＡＴＯ粉体和占ＡＴＯ粉体重量２～１０％的分散剂组成。制备时，将纳米ＡＴＯ粉体，醇类溶剂和分散剂在搅拌或超声波的作用下进行预分散，然后对此预分散体进行研磨分散，制得油性ＡＴＯ隔热浆料。纳米油性ＡＴＯ隔热浆料制备的透明无机硅隔热涂料是由透明无机硅涂料与纳米油性ＡＴＯ隔热浆料组成，透明无机硅涂料与纳米油性ＡＴＯ隔热浆料的重量比为３∶１～１∶１。本发明专利技术制备的涂料具有较好的隔热效果，较高的硬度和透明性，耐候性好，且具有一定的防火效果。

Nano oily ATO heat insulation slurry and preparation method and application thereof

The invention discloses a nano oily ATO heat insulating slurry, a preparation method and an application thereof. In weight fraction, the slurry is composed of 67~90 alcohols, 10~30 nanometer ATO powders and 2 ATO of 10% wt% powder. During the preparation of nano ATO powder, alcohol solvent and dispersant in stirring or ultrasonic wave pre dispersed, then pre DISPPERSANTS grinding dispersion, prepared ATO slurry oil. Transparent heat insulation coating of nano inorganic silicon oil ATO slurry preparation is composed of transparent inorganic silicon coating and nano ATO slurry oil, transparent inorganic silicon coating and nano ATO slurry oil weight ratio of 3: 1 to 1: 1. The paint prepared by the invention has better heat insulation effect, higher hardness and transparency, good weather resistance, and certain fire prevention effect.

【技术实现步骤摘要】

本专利技术涉及一种玻璃隔热所述的用的纳米透明无机硅隔热涂料，该涂料能 改善玻璃的隔热性能，尽量多让可见光透过，而不致对室内采光有太大影响， 而且耐候性好，硬度高。
技术介绍
随着科学技术与社会生产的快速发展，能源和环境成为全社会日益瞩目的 两大问题，从而为节能和环保提出了更高要求。建筑隔热(绝热)保温是节约能 源、提高建筑物居住和使用功能的一个重要方面。建筑能耗在人类整个能源消 耗中所占比例一般在30% 40%，且其中绝大多数是采暖和空调的能耗，故建 筑节能意义重大。据研究统计，在建筑能耗方面，我国建筑门窗散热量占建筑 外围总散热量的50%以上，为发达国家的3 5倍。因此提高门窗的保温隔热 性能是降低建筑能耗的有效途径。太阳光中除了可见光外还含有紫外线和红外 线，特别是近红外线被称为热线。较为理想的隔热涂料能阻隔近红外线透过， 而让尽可能多的可见光透过，不致过多影响室内采光。目前市面上的隔热玻璃产品有低辐射镀膜玻璃和各种各样的玻璃贴膜以 改善玻璃的隔热性能。低辐射镀膜玻璃生产工艺比较复杂，而且工艺设备投资 比较大。虽然具有较好的节能效果，但价格较高，难以为广泛推广应用，且不 适用于本文档来自技高网...

【技术保护点】
一种纳米油性ＡＴＯ隔热浆料，其特征在于，以重量份数计，该浆料由６７～９０份醇类溶剂，１０～３０份纳米ＡＴＯ粉体和占ＡＴＯ粉体重量２～１０％的分散剂组成。

【技术特征摘要】

【专利技术属性】
技术研发人员：孟庆林，李宁，
申请(专利权)人：华南理工大学，
类型：发明
国别省市：81[中国|广州]