The invention discloses a carbon nanotube modified conductive anticorrosive coating for grounding grids, belonging to the technical field of conductive coating. It mainly comprises the following raw materials according to the mass fraction meter: nano powder filler 25-27, epoxy resin, 30-32 parts of nano magnetic iron oxide 22-25, inert diluent 12-14 parts, polyurethane resin, alkyd resin, 6-8 15-17, 6-7 10-11, ethyl acetate, polyvinyl alcohol, dispersing agent 2, 11-13, methyl acetone isobutyl ketone 12-13 parts, three 2-2.5 butyl phosphate. The invention has the advantages of low raw material and reasonable compatibility, and has good corrosion resistance and conductivity. The invention is mainly used for carbon nanotubes of grounding grids.
【技术实现步骤摘要】
一种接地网的碳纳米管改性导电防腐涂料
本专利技术属于导电涂料
,具体地说,尤其涉及一种接地网的碳纳米管改性导电防腐涂料。
技术介绍
接地网是发电厂、变电站、输电线路灯电力设备中,确保工作接地、防雷接地、保护接地的必要安全设施。在输电、配电、变电等电力系统中,要求接地网与大地的接触电阻越小越好,如果接地网受到严重腐蚀,带电设备在运行时就会发生短路而烧断接地网,导致电位升高,造成人身设备事故。开发具有防腐蚀性和导电功能的涂料为解决接地材料的腐蚀问题提供了新途径。目前,现有的导电涂层耐腐蚀性能差,而耐腐蚀性能较好的防腐涂层导电性能又很低,急需开发一种兼具防腐与导电的涂料。
技术实现思路
本专利技术的目的在于克服上述缺陷,提供一种接地网的碳纳米管改性导电防腐涂料,其原料低廉、配伍合理,兼具较好的防腐与导电性能。所述的接地网的碳纳米管改性导电防腐涂料,包括按照质量份数计的如下原料:纳米碳粉填料25-27份、环氧树脂基体30-32份、纳米磁性氧化铁22-25份、惰性稀释剂12-14份、聚氨酯树脂6-8份、醇酸树脂15-17份、聚乙烯醇6-7份、乙酸乙酯10-11份、分散剂2份、丙酮11-13份、甲基异丁基酮12-13份、磷酸三丁酯2-2.5份。进一步的,包括按照质量份数计的如下原料:纳米碳粉填料25份、环氧树脂基体30份、纳米磁性氧化铁22份、惰性稀释剂12份、聚氨酯树脂6份、醇酸树脂15份、聚乙烯醇6份、乙酸乙酯10份、分散剂份、丙酮11份、甲基异丁基酮12份、磷酸三丁酯2份。进一步的,包括按照质量份数计的如下原料:纳米碳粉填料27份、环氧树脂基体32份、纳米磁性 ...
【技术保护点】
一种接地网的碳纳米管改性导电防腐涂料,其特征在于:包括按照质量份数计的如下原料:纳米碳粉填料25‑27份、环氧树脂基体30‑32份、纳米磁性氧化铁22‑25份、惰性稀释剂12‑14份、聚氨酯树脂6‑8份、醇酸树脂15‑17份、聚乙烯醇6‑7份、乙酸乙酯10‑11份、分散剂2份、丙酮11‑13份、甲基异丁基酮12‑13份、磷酸三丁酯2‑2.5份。
【技术特征摘要】
1.一种接地网的碳纳米管改性导电防腐涂料,其特征在于:包括按照质量份数计的如下原料:纳米碳粉填料25-27份、环氧树脂基体30-32份、纳米磁性氧化铁22-25份、惰性稀释剂12-14份、聚氨酯树脂6-8份、醇酸树脂15-17份、聚乙烯醇6-7份、乙酸乙酯10-11份、分散剂2份、丙酮11-13份、甲基异丁基酮12-13份、磷酸三丁酯2-2.5份。2.根据权利要求1所述的接地网的碳纳米管改性导电防腐涂料,其特征在于:包括按照质量份数计的如下原料:纳米碳粉填料25份、环氧树脂...
【专利技术属性】
技术研发人员:廖善坤,
申请(专利权)人:国网山东郯城县供电公司,国家电网公司,
类型:发明
国别省市:山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。