The invention discloses a polyurethane waterproof coating is coated on the transmission line, belonging to the cable with waterproof ability of polyurethane waterproof coating, in order to solve the transmission cable with good waterproof ability demand. Polyurethane waterproof coating of the invention comprises the following components: weight of polyurethane resin 8-15, epoxy resin 5-20, barium sulfate 5-10, carbon fiber 2-6, nano 1-1.5, nano magnesium hydroxide aluminum hydroxide 0.5-1, propylene glycol 1-2. Polyurethane waterproof coating of the invention, the production method is simple, the various components can be mixed; performance of coatings produced by stable coating on the cable appearance, can form a bright and transparent, good softness, coating and has a certain mechanical strength, water resistance, resistance of the layer has the advantages of good performance of chemical solvents.
【技术实现步骤摘要】
一种聚氨酯防水涂料
本专利技术涉及一种防水涂料，具体地说，涉及一种输电线缆外的防水涂料。
技术介绍
电缆，尤其是在地下如海底的电缆，需要有较好的防水性能，水分一旦侵入电缆内部，电缆将会受到破坏而无法使用。水分的侵入方式一般有两种：从电缆端部、电缆表面强度较弱的地方。现有的电缆防水的措施是采用阻水带缠绕或者采用阻水填料填充，一旦有水分侵入，在水分侵入口的填充材料吸水膨胀直接将水分侵入口堵住。但是这种方法依然存在缆芯被浸入水分的风险。
技术实现思路
为解决上述问题，本专利技术提供一种涂覆在输电线缆外的具有防水能力的聚氨酯防水涂料。本专利技术所述的聚氨酯防水涂料，包括下列重量份的组份：聚氨酯树脂8-15份、环氧树脂5-20份、硫酸钡5-10份、碳纤维2-6份、纳米氢氧化铝1-1.5份、纳米氢氧化镁0.5-1份，丙二醇1-2份。优选的，所述聚氨酯防水涂料包括下列重量份的组份：聚氨酯树脂10份、环氧树脂15份、硫酸钡5份、碳纤维6份、纳米氢氧化铝1份、纳米氢氧化镁1份，丙二醇2份。优选的，所述聚氨酯防水涂料还包括盐酸，所述盐酸的质量份数为37％，质量分数为37％的盐酸的用量满足质量比：盐酸：环氧树脂＝4-8：1-3。与现有技术相比，本专利技术的有益效果是：首先制作方法简单，将多种组份混合即可；制作而成的涂料性能稳定，涂覆在线缆的外表，能够形成光亮透明、柔软性好，且具有一定机械强度的涂层，该图层具有耐水、耐化学溶剂性能好的优点。具体实施方式下面结合实施例对本专利技术做进一步解释。实施例1一种聚氨酯防水涂料，包括下列重量份的组份：聚氨酯树脂10份、环氧树脂15份、硫酸钡5份...
【技术保护点】
一种聚氨酯防水涂料，其特征在于，包括下列重量份的组份：聚氨酯树脂8‑15份、环氧树脂5‑20份、硫酸钡5‑10份、碳纤维2‑6份、纳米氢氧化铝1‑1.5份、纳米氢氧化镁0.5‑1份，丙二醇1‑2份。
【技术特征摘要】
1.一种聚氨酯防水涂料，其特征在于，包括下列重量份的组份：聚氨酯树脂8-15份、环氧树脂5-20份、硫酸钡5-10份、碳纤维2-6份、纳米氢氧化铝1-1.5份、纳米氢氧化镁0.5-1份，丙二醇1-2份。2.根据权利要求1所述的聚氨酯防水涂料，其特征在于，包括下列重量份的组份：聚...
【专利技术属性】
技术研发人员：樊旭东，
申请(专利权)人：国网山东郯城县供电公司，国家电网公司，
类型：发明
国别省市：山东,37