The invention discloses a magnetic slurry, a preparation method thereof and a preparation method of a magnetic sheet. A magnetic slurry, including magnetic powder and organic carrier, the mass of the powder and the organic carrier ratio of 1:0.7 to 1:0.9; the organic carrier in weight percentage: 8% to 10% including binder, 82% ~ 90% and 0.1% ~ 1% of the solvent, defoaming agent, dispersing agent 0.1% ~ 1% and 1% ~ 6% of the plasticizer, the adhesive for polyvinyl butyral, the solvents including alcohols and esters solvent solvent. The magnetic slurry is not easy to crack when casting, and the Q value of the magnetic sheet is higher.
【技术实现步骤摘要】
磁性浆料、其制备方法及磁片的制备方法
本专利技术涉及一种磁性浆料、其制备方法及磁片的制备方法。
技术介绍
随着电子通讯行业的发展，NFC不断发展成熟，越来越多的手机配置了NFC功能，NFC模块已经成为手机的出厂标配，NFC芯片中含有NFC天线，实际应用中，手机中的金属部件如电池和手机后盖会对信号造成干扰，这些金属件使通讯距离和灵敏程度大打折扣，甚至无法工作。在NFC天线和金属之间放上一块磁片，它可以将磁力线吸收到天线附近而不通过那些金属部件。磁片由磁性浆料制备而成。磁性浆料包括磁粉及有机载体，有机载体含有粘结剂以方便成型，粘结剂在排胶时挥发。磁性浆料中，有机载体中含有15％～20％的粘结剂，粘结剂含量过高时，导致磁片排胶不彻底，在随后的烧结工艺中收缩率高，气孔量高，造成磁片损耗高且容易变形，如果降低粘结剂的含量，则在磁性浆料流延成型时容易开裂。
技术实现思路
基于此，有必要提供一种流延成型时不易开裂且磁片Q值较高的磁性浆料、其制备方法及瓷片的制备方法。一种磁性浆料，包括磁粉及有机载体，所述磁粉与所述有机载体的质量比为1：0.7～1：0.9；所述有机载体以质量百分比计，...
【技术保护点】
一种磁性浆料，其特征在于，包括磁粉及有机载体，所述磁粉与所述有机载体的质量比为1：0.7～1：0.9；所述有机载体以质量百分比计，包括：8％～10％的粘结剂，82％～90％的溶剂，0.1％～1％的消泡剂，0.1％～1％的分散剂和1％～6％的增塑剂，所述粘结剂为聚乙烯醇缩丁醛，所述溶剂包括醇类溶剂及酯类溶剂。
【技术特征摘要】
1.一种磁性浆料，其特征在于，包括磁粉及有机载体，所述磁粉与所述有机载体的质量比为1：0.7～1：0.9；所述有机载体以质量百分比计，包括：8％～10％的粘结剂，82％～90％的溶剂，0.1％～1％的消泡剂，0.1％～1％的分散剂和1％～6％的增塑剂，所述粘结剂为聚乙烯醇缩丁醛，所述溶剂包括醇类溶剂及酯类溶剂。2.根据权利要求1所述的磁性浆料，其特征在于，所述溶剂包括无水乙醇、醋酸正丙酯、正丁醇及尼龙酸二甲酯。3.根据权利要求2所述的磁性浆料，其特征在于，所述无水乙醇、醋酸正丙酯、正丁醇及尼龙酸二甲酯的质量比1:2～3:1～1.5:0.5～1。4.根据权利要求1所述的磁性浆料，其特征在于，所述磁粉选自镍锌铁氧体磁粉及锰锌铁氧体磁粉中的至少一种；及/或，所述磁粉的粒度D50为0.8μm～1.2μm。5.根据权利要求1所述的磁性浆料，其特征在于，所述增塑剂选自邻苯二甲酸二辛酯、硬脂酸丁酯、聚乙二醇及聚乙二醇衍生物中的至少一种；及/或，所述分散剂选自蓖麻油、脂肪酸及磷酸酯中的至少一种。6.根据权利要求1...
【专利技术属性】
技术研发人员：关旺，黄昆，戴燕城，
申请(专利权)人：广东风华高新科技股份有限公司，风华研究院广州有限公司，
类型：发明
国别省市：广东,44