本发明专利技术提供一种熔解装置，其用于在每单位时间的熔融玻璃的流出量少的玻璃预成型坯的制造过程中，供给均匀性高的熔融玻璃。在熔融槽１２的内部，搅拌叶片１４４旋转，在熔融玻璃Ａ的熔融液中引起对流。由此，使滞留在熔融玻璃Ａ的一部分的成分扩散到整个熔融玻璃Ａ中，从而可以获得均匀的熔融玻璃Ａ。然而，对于暂时变得均匀的熔融玻璃Ａ而言，因为长时间处于已熔解的状态，所以会产生条纹。将含条纹的熔融玻璃Ａ的一部分送至剪切搅拌室１２４，利用剪切搅拌来对熔融玻璃Ａ进行搅拌。由此，将含条纹等不均匀部分的一部分熔融玻璃Ａ剪切得较细，从而可以获得整体上均匀的熔融玻璃Ａ。

Melting device

The present invention provides a fusing apparatus for supplying molten glass of high uniformity in the manufacture of glass preforms during the flow of molten glass per unit time. In the interior of the molten groove 12, the stirring blade 144 rotates to cause convection in the molten liquid of molten glass A. As a result, a portion of the component remaining in the molten glass A is diffused throughout the molten glass A so that a homogeneous molten glass A can be obtained. However, for a temporarily homogeneous molten glass, A produces streaks because it is in a fused state for a long time. A portion of the Striped molten glass A is sent to the shear chamber 124, and the molten glass A is stirred by shearing agitation. Thus, a part of molten glass A with an uneven part such as a stripe is cut finer so that a homogeneous fused glass A can be obtained on the whole.

【技术实现步骤摘要】

本专利技术涉及具有均匀搅拌熔融玻璃的搅拌设备的熔解装置。
技术介绍
用于光学元件等的玻璃预成型坯(玻璃料滴)是通过如下方式而获得的，即，利用熔解装置来熔解原料，使所获得的熔融玻璃成形为适当大小的玻璃块。此处，作为在玻璃预成型坯的制造过程中所使用的熔解方法，众所周知的是连续熔解法和分批熔解法。在进行连续熔解时，可以在各个具有不同功能的单个层中连续地进行原料的放入、熔解、净化、和搅拌，因此适合大量生产玻璃预成型坯的情形等。另一方面，在进行分批熔解时，在单一的槽中分批地进行原料的放入、熔解、净化、和搅拌，适合生产总产量较少的玻璃预成型坯的情形等。玻璃预成型坯的制造中，重要的是精确地制造均匀且具有固定光学特性的玻璃预成型坯。因此，除了选择适当的原料之外，还必须在原料玻璃的熔解、净化、和搅拌的阶段进行各种考虑。特别在利用分批熔解来供给熔融玻璃时，因分多次放入原料，所以容易引起加热过程的不均匀，或者容易在熔解容器内产生加热过程的不均匀，从而成为导致玻璃预成型坯的光学特性变得不稳定的原因之一。为了解决上述问题，以前采用的是如下方法，即，利用具有搅拌叶片的搅拌器具，在熔融玻璃中引起对流，并加以搅本文档来自技高网...

【技术保护点】
一种熔解装置，其特征在于包括：对流搅拌室，其使熔融玻璃对流；和剪切搅拌室，其对上述熔融玻璃进行剪切。

【技术特征摘要】
...

【专利技术属性】
技术研发人员：中山彻，青木哲也，妹尾龙也，
申请(专利权)人：株式会社小原，
类型：发明
国别省市：JP[日本]