The invention relates to a titanium dioxide promoted four oxidation cobalt catalyst and its preparation and application. Take 3.0g TiO2 5mL TiO2 impregnated with 1.1g containing cobalt nitrate hydrate (Co (NO3) 2 - 6H2O) in aqueous solution, stirring, ultrasonic impregnation 30min, 20 80 C 300 C 200 drying, roasting 3 6h, to obtain the required product. The catalytic activity and stability of propane catalyzed by Co3O4 (TiO2) and four cobalt oxide (Co3O4) were increased by. The introduction of Trace Potassium can further improve the activity of the catalyst. The method is economical, simple, and has good application prospect.
【技术实现步骤摘要】
本专利技术涉及纳米催化剂
,尤其是涉及二氧化钛促进的四氧化三钴催化剂及其制备和应用。
技术介绍
随着人们生活质量的提高,环境污染问题受到了越来越多的关注。碳氢化合物(HC)能够与氮氧化物(NOx)发生光化学反应,导致光化学烟雾污染,对人类健康和生态环境造成严重的影响。因此,HC的治理问题亟待解决。HC的光催化分解是一种绿色、节能、环保的首选方法,但是其效率很低。HC常温吸附,因吸附材料易饱和,再生过程中可能引起二次污染等,限制了该方法的使用。HC催化燃烧产物为二氧化碳和水,是一种理想的解决HC污染的方法。目前,HC催化燃烧的催化剂以担载型贵金属最为普遍,但这类催化剂价格昂贵,较难工业化应用。四氧化三钴(Co3O4)的HC催化燃烧活性仅次于贵金属催化剂,并且成本相对低廉,具有很好的应用前景。然而,Co3O4抗烧结性能较差,重复利用性差。选择合适的载体和制备方法,不仅能够提高Co3O4的抗烧结性能,而且可以维持Co3O4的高活性,促进其工业化应用。
技术实现思路
为克服现有技术的不足,本专利技术采用二氧化钛(TiO2)作为载体,以提高四氧化三钴(Co3O4)催化性能;并以丙烷为模拟污染物,对催化剂进行了HC催化燃烧性能研究。通过载体TiO2与Co3O4的协同作用,提高Co3O4的活性和稳定性。一种二氧化钛促进的四氧化三钴催化剂的制备方法,其特征在于,称取3.0g 二氧化钛TiO2浸渍于5mL含有1.1g硝酸钴水合物(Co(NO3)2·6H2O)的水溶液中,搅拌均匀后,超声浸渍30min,20-80℃烘干,200-300℃焙烧3-6h,得到所需产物。微量钾的 ...
【技术保护点】
一种二氧化钛促进的四氧化三钴催化剂的制备方法,其特征在于,称取3.0g 二氧化钛TiO2浸渍于5mL含有1.1g硝酸钴水合物(Co(NO3)2·6H2O)的水溶液中,搅拌均匀后,超声浸渍30min,20‑80℃烘干,200‑300℃焙烧3‑6h,得到所需产物。
【技术特征摘要】
1.一种二氧化钛促进的四氧化三钴催化剂的制备方法,其特征在于,称取3.0g 二氧化钛TiO2浸渍于5mL含有1.1g硝酸钴水合物(Co(NO3)2·6H2O)的水溶液中,搅拌均匀后,超声浸渍30min,20-80℃烘干,200-300℃焙烧3-6h,得到所需产物。2.根据权利要求1所述一种二氧化钛促进的四氧化三钴催化剂的制备方法,其特征在于,微量钾的引入,可以进一步提高催化剂的活性,具体为:称取...
【专利技术属性】
技术研发人员:何丹农,
申请(专利权)人:上海纳米技术及应用国家工程研究中心有限公司,
类型:发明
国别省市:上海;31