Since the development of plastics industry because of its high corrosion resistance and insulation, thus replacing the traditional metal in some areas, polyamide 6 (PA6) engineering plastics with excellent mechanical properties and electrical properties, also has the wear resistance, oil resistance, self lubrication, corrosion resistance and good processing performance and other advantages of its use; more and more widely, including the application of automobile, machinery and equipment, electronic and electrical appliances, chemical equipment, construction, household goods, transportation etc.. The present invention provides a method for preparing polyamide thermal conductive modified material without affecting the mechanical properties of the material and enhancing the thermal conductivity of the polyamide material.
【技术实现步骤摘要】
一种聚酰胺导热改性材料
本专利技术属聚酰胺PA6材料生产技术，具体的说是一种聚酰胺导热改性材料及其制备方法。
技术介绍
塑料行业发展至今因其具有高抗腐蚀性及绝缘性，从而在一些领域中替代了传统金属，聚酰胺6(PA6)工程塑料具有优良的力学性能和电性能，还具有耐磨、耐油、自润滑、耐腐蚀以及良好的加工性能等优点；其用途也越来越广泛,应用范围包括汽车、机械设备、电子电器、化工设备、建筑、生活用品、交通运输等。
技术实现思路
本专利技术的目的在于提供一种聚酰胺导热改性材料及其制备方法。聚酰胺导热改性材料的原料按质量百分比配比为：聚酰胺PA6：50、氧化镁(10-12um)：50、抗氧剂(乙烯-辛烯的共聚物)：1.5、着色剂：1.0、分散润滑剂(TAS-2A)：1.0。所述聚酰胺导热改性材料的制备方法为：将各种原料在高速混合器中干混15-20分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为160-180℃，二区为230-250℃，三区为255-275℃，四区为250-270℃；五区为230-250℃，停留时间为1-2分钟，压力为10-15Mpa。具体实施方式实施例(1)所述聚酰胺导热改性材料的原料按质量百分比配比为：聚酰胺PA6：50、氧化镁(10-12um)：50、抗氧剂(乙烯-辛烯的共聚物)：1.5、着色剂：1.0、分散润滑剂(TAS-2A)：1.0。(2)所述材料的制备方法为：将各种原料在高速混合器中干混15-20分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为160-180℃，...
【技术保护点】
一种聚酰胺导热改性材料，其特征在于，原料按质量百分比配比为：聚酰胺PA6：50、氧化镁(10‑12um)：50、抗氧剂(乙烯‑辛烯的共聚物)：1.5、着色剂：1.0、分散润滑剂(TAS‑2A)：1.0。
【技术特征摘要】
1.一种聚酰胺导热改性材料，其特征在于，原料按质量百分比配比为：聚酰胺PA6：50、氧化镁(10-12um)：50、抗氧剂(乙烯-辛烯的共聚物)：1.5、着色剂：1.0、分散润滑剂(TAS-2A)：1.0。2.根据权利要求1所述的聚酰胺导热改性材料，其特征在于，所述材料的制备方法为：将...
【专利技术属性】
技术研发人员：张瑞仙，
申请(专利权)人：山东天富非织造材料有限公司，
类型：发明
国别省市：山东,37