The invention discloses a silver black foam agent, which comprises the following components by weight: 3 dimercaptopropanol 5 copies, 5 copies of 2 sodium sulfide, sodium hypophosphite 1 ellagic acid 3, 1 2 copies, 15 copies of 12 oilofpine, potassiumperfluorooctane-1-sulphonate 12 15 20 copies, 25 copies of water, the preparation method is as follows: the dimercaptopropanol and pine oil in the container mix, then add potassiumperfluorooctane-1-sulphonate and water, stirring for 15 20min, finally adding the sodium sulfide, sodium hypophosphite and ellagic acid, stirring 5 10min can be. The foaming agent has the advantages of convenient use, good black effect and stable storage.
【技术实现步骤摘要】
本专利技术涉及特色银器领域,具体涉及一种银器发黑泡沫剂及其制备方法。
技术介绍
乌银是在银首饰上把银、硫的混合物融化,并以玻璃质状态形成覆盖层。乌银覆盖层疏松乌黑,与白银的光洁银白形成鲜明对比,产生特殊的视觉效果。由于经过了特殊的防旧处理,乌银首饰不仅长期不变色,表面硬度也大大增强,别具一格的质感和色泽,使这种首饰粗犷而古朴,受到很多时尚人士的喜爱。现有技术制作乌银大多工艺复杂,成本较高,寻找一些简便可行且无污染的方法制作乌银成为许多科研工作者的研究对象,如中国专利申请201510023846.1公开了一种银器发黑剂,包括硫化钠1~3份,蛋氨酸2~5份,硫脲1~3份,氯化铵或硫酸铵1~5份,柠檬酸钠1~5份,硫酸钠10~20份,六偏磷酸钠1~2,十二烷基硫酸钠0.1~0.2份,该银器发黑剂为粉末剂,使用时需加水溶解成25~35%的水溶液,使用稍显不便。
技术实现思路
基于以上技术现状,本专利技术的目的是提供一种使用方便、发黑效果好且储存稳定的银器发黑泡沫剂,并进一步提供其制备方法。本专利技术采用以下技术方案:一种银器发黑泡沫剂,其包括以下重量份的组分:二巯基丙醇3-5份,硫化钠2-5份,次亚磷酸钠1-3份,鞣花酸1-2份,松醇油12-15份,全氟辛烷磺酸钾12-15份,水20-25份。优选地,所述各组分的重量份数为:二巯基丙醇3份,硫化钠3份,次亚磷酸钠2份,鞣花酸1份,松醇油15份,全氟辛烷磺酸钾15份,水25份。所述的银器发黑泡沫剂的制备方法为:将所述二巯基丙醇和松醇油在容器中搅拌混合,再加入全氟辛烷磺酸钾和水,搅拌15-20min,最后加入所述硫化钠、 ...
【技术保护点】
一种银器发黑泡沫剂,其特征在于:其包括以下重量份的组分:二巯基丙醇3‑5份,硫化钠2‑5份,次亚磷酸钠1‑3份,鞣花酸1‑2份,松醇油12‑15份,全氟辛烷磺酸钾12‑15份,水20‑25份。
【技术特征摘要】
1.一种银器发黑泡沫剂,其特征在于:其包括以下重量份的组分:二巯基丙醇3-5份,硫化钠2-5份,次亚磷酸钠1-3份,鞣花酸1-2份,松醇油12-15份,全氟辛烷磺酸钾12-15份,水20-25份。2.根据权利要求1所述的银器发黑泡沫剂,其特征在于:所述各组分的重量份数为:二巯基丙醇3份,硫化钠3份,次亚磷酸钠2份,鞣花酸1份,松醇油...