The invention relates to a method for preparing aluminum mesh with carbon film collector, which is characterized in that: the viscosity of the organic material as carbon source, the evenly on the surface of the aluminum mesh, then at a certain temperature of the carbonization of organic matter, carbon film formed on aluminum net gap. The fluid in the gap within the aluminum mesh coated with a layer of carbon film, while reducing the weight of the traditional aluminum foil collector can increase the binding force between the cathode material and the collector, the carbon film aluminum mesh preparation process is simple, and light quality, increase the surface area of aluminum mesh.
【技术实现步骤摘要】
本专利技术涉及，属于电池
。
技术介绍
锂离子二次电池是一种优秀的能量存储和转换的器件，已经在人们生产和生活中的各个领域得到了广泛应用。传统的锂离子电池采用铝箔作为电池正极的集流体，质量较重，而且正极材料与集流体之间的结合力较差，在涂布完成后会出现材料脱落等问题。检索专利发现，还没有发现采用同类方法制备集流体用碳膜铝网的相关专利。
技术实现思路
本专利技术的目的是提供，其在铝网集流体的缝隙内涂覆一层碳膜，作为锂离子电池集流体，降低传统铝箔集流体的重量的同时可以增加正极材料与集流体之间的结合力，碳膜铝网制备工艺简单，并且质量轻、增加铝网的表面积。本专利技术的技术方案是这样实现的:，其特征在于具体步骤如下: (1)选取一定质量葡萄糖、聚乙烯吡咯烷酮、聚偏氟乙烯等有机碳源，溶于水、氮甲基吡咯烷酮等溶剂中当中，在25°c ~100°c温度下，配制成形成浓度在30 g/L^200g/L的粘稠状浆料； (2)使用拉浆的方法，将(I)中所得到的粘稠状浆料涂于铝网表面； (3)在25°C~110°C温度下，在空气氛或者氩气、氮气氛下烘干浆料，在铝网表面得...
【技术保护点】
一种集流体用碳膜铝网的制备方法，其特征在于具体步骤如下：1）选取一定质量葡萄糖、聚乙烯吡咯烷酮、聚偏氟乙烯等有机碳源，溶于水、氮甲基吡咯烷酮等溶剂中当中，在25℃~100℃温度下，配制成形成浓度在30?g/L~200g/L的粘稠状浆料；2）使用拉浆的方法，将（1）中所得到的粘稠状浆料涂于铝网表面；3）在25℃~110℃温度下，在空气或者氩气、氮气下烘干浆料，在铝网表面得到一层50~500μm厚度的有机物膜；之后将铝网置于惰性或者还原性气体中并在300~400℃加热碳化2~4小时，使有机物薄膜碳化，之后冷却即得到碳膜铝网。
【技术特征摘要】
1.一种集流体用碳膜铝网的制备方法，其特征在于具体步骤如下: 1)选取一定质量葡萄糖、聚乙烯吡咯烷酮、聚偏氟乙烯等有机碳源，溶于水、氮甲基吡咯烷酮等溶剂中当中，在25°c ~100°c温度下，配制成形成浓度在30 g/L^200g/L的粘稠状浆料； 2)使用拉浆的方法，将(...
【专利技术属性】
技术研发人员：姜涛，陈慧明，张克金，王丹，崔新然，
申请(专利权)人：中国第一汽车股份有限公司，
类型：发明