The invention discloses a titanium carbide - tungsten carbide hard phase hard alloy, including as hard phase titanium carbide alloy - tungsten carbide mixture, as the binder phase of Fe3Al alloy and Mo alloy, the tungsten carbide hard phase for 50%~90% quality percentage; the particle size of 5~8 m; titanium carbide alloy for hard phase the mass percentage of 10%~50%, the particle size of 1~3 M. The percentage of Fe3Al alloy in cemented carbide is 5.5%~15%, and the percentage of Mo in cemented carbide is 0.5%~1%. In the invention, the bonding phase and hard phase with good wettability, the alloy can provide high strength and high performance caused by density, corrosion resistance and wear resistance and good machining, heat treatment and welding parts, but also make the same type of hard alloy to reduce the cost of preparation.
【技术实现步骤摘要】
一种碳化钛-碳化钨复合硬质合金
本专利技术属于硬质合金领域，涉及一种复合硬质相硬质合金。
技术介绍
磨损是材料失效的原因之一。据相关数据统计，设备损坏和材料失效中有超过70% 部分是由于磨损所致，每年全世界由于磨损所导致的直接和间接损失达到了数千亿元。因此高强度、高致密度、耐腐蚀、耐磨损等综合性能良好的结构部件成为了迫切需要。在现有的热处理钢、奥氏体钢、高铬铁钢和硬质合金四类耐磨材料中，硬质合金具有最好的耐磨性，特别是WC-Co硬质合金兼具高耐磨性和良好的韧性已广泛的使用在切削工具、耐磨零件、采矿与筑路工程机械等领域。但由于WC-Co硬质合金的粘结相Co属于战略资源，价格不断上涨，因此寻找Co的代用材料和新型硬质合金的开发成为当务之急的任务。TiC是过渡金属碳化物中的一种具有面心立方结构的间隙相，具有高硬度、高熔点、低密度、热稳定性以及烧结过程中晶粒长达趋势小等特点，是新型硬质合金的开发的材料之一。以TiC作为硬质相的合金和钢材相比具有钢材无法比拟的高硬度、高耐磨性和淬透性，和一般硬质合金相比具有可机械加工、可热处理和可焊接等优点。但另一方面以TiC作为硬质相的合...
【技术保护点】
一种碳化钛?碳化钨复合硬质合金，其特征在于，该硬质合金包括作为硬质相的碳化钛合金?碳化钨合金混合物、作为粘结相的Fe3Al合金和金属Mo，所述碳化钛合金?碳化钨合金混合物中，包括占硬质相质量百分比50%~90%、粒径5~8μm的碳化钨合金和占硬质相质量百分比10%~50%、粒径1~3μm的碳化钛合金；所述Fe3Al合金占硬质合金的质量百分比为5.5%~15%，所述Mo占硬质合金的质量百分比为0.5%~1%，所述Fe3Al合金的成分为：Al??17%~20%；Cr??1.3%~1.9%；Nb??2.0%~2.4%；Zr??0.3%~0.5%；B???0.1%~0.3%；Ce?...
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。