改性尖晶石锰酸锂材料、制备方法及包括其的电池用正极材料技术

本发明专利技术公开了一种改性尖晶石锰酸锂材料、制备方法及包括其的电池用正极材料。其中，改性尖晶石锰酸锂材料中掺杂有钒元素，Li∶Mn∶V的摩尔比为0.96～1.12∶1.80～2∶0.001～0.05。本发明专利技术提供的改性尖晶石锰酸锂材料，结构稳定、形貌规整、加工性能优异并具有良好的电化学性能；本发明专利技术提供的改性尖晶石锰酸锂材料的制备方法，所采用的高温固相合成法，成本低廉、流程简单、参数控制范围宽泛，适合于大规模工业化生产。

Modified spinel lithium manganate material, preparation method and positive electrode material for battery

The invention discloses a modified spinel lithium manganate material, a preparation method and a positive electrode material for the battery. Among them, the molar ratio of vanadium doped in the modified spinel lithium manganate material is Li to Mn: V molar ratio is from 0.96 to 1.12 to 1.80 to 2: 0.001 to 0.05. Instead of lithium manganese spinel material provided by the invention, stable structure, morphology, and excellent processing performance with good electrochemical performance; modified spinel lithium manganate material prepared by the method provided by the invention, the high temperature solid phase synthesis method, low cost, wide range of control parameters, Cheng Jiandan flow, which is suitable for large scale industrial production.

【技术实现步骤摘要】

本专利技术涉及一种尖晶石锰酸锂材料及其制备方法，具体而言，涉及一种V元素微量掺杂的改性尖晶石锰酸锂材料及其制备方法，以及由改性尖晶石锰酸锂材料制成的电池用正极材料。
技术介绍
近年来，锂离子电池正极材料已经从单一的钴酸锂材料，发展到钴酸锂、锰酸锂、 镍酸锂、三元材料、磷酸铁锂等多种材料多元应用的阶段。钴酸锂、三元材料合成时需要大量资源稀缺、价格昂贵的金属钴，因而原材料成本高；充电态的钴酸锂、镍酸锂的热稳定性差，使得以其为正极材料的电池在滥用条件下的安全性欠佳；三元材料、磷酸铁锂的电压平台低，使得其无法满足越来越高的工作电压要求。而尖晶石锰酸锂，具有资源广泛、价格低廉、充放电平台高、滥用情况下安全性好等优点，逐步成为下一代锂离子电池特别是动力锂离子电池的首选的正极材料。但是，尖晶石锰酸锂普遍存在体积比能量低、高温循环性能差等缺点，提高体积比能量和改善高温循环性能是尖晶石锰酸锂的科研发展方向。目前，通常通过提高材料密度的方法来提高尖晶石锰酸锂的体积比能量，如中国专利技术专禾U CN200410096259. 7、CN200410009004. 2、CN200610140909. 2、C本文档来自技高网...

【技术保护点】
１．一种改性尖晶石锰酸锂材料，其特征在于，所述改性尖晶石锰酸锂材料中掺杂有钒元素，其中，Ｌｉ∶Ｍｎ∶Ｖ的摩尔比为０．９６～１．１２∶１．８０～２∶０．００１～０．０５。

【技术特征摘要】

【专利技术属性】
技术研发人员：刘爱强，李碧平，许国强，邹敏，熊学，涂文，
申请(专利权)人：湖南美特新材料科技有限公司，
类型：发明
国别省市：43