The invention belongs to the field of organic material technology, and relates to a preparation method for conductive polymer sheath material, conductive polymer sheath material ingredients according to the mass percentage of thermoplastic polymer resin 60-30%, nano 25-30% conductive carbon black, conductive carbon fiber or conductive agent 5-14%, toughening agent 10-18%, processing aid for 0.5-1.5% the mixture of 1-3% and dispersant; the components of raw materials are mixed, stirred, twin-screw extruder, extrusion, cooling, granulating, drying and packaging products; or adding a mixture of components of the raw material to the mixer for mixing, kneading, fully dispersed by double roller mill mixing and rolling into sheets produced by single screw extruder, extrusion, cooling, granulating, drying and packaging materials to form products, the process is simple, The material has good electrical performance, low cost and friendly production environment.
【技术实现步骤摘要】
本专利技术属于有机材料
，涉及一种导电高分子护套组合材料的制备技术方法，用于铁路贯通地线场合的电线电缆材料，特别是一种铁路贯通用的导电高分子护套材料的制备方法，其导电高分子护套包括设置在防腐导电涂层外的第一次挤制的内层护套和位于内层护套外围的第二次挤制的外层护套。
技术介绍
随着铁路的高速发展，铁道专用通讯信号正向着现代化、数字化的方向快速发展， 从而对信号系统接地可靠性也提出了更高的要求，所以，综合贯通地线电缆应运而生。综合贯通地线电缆是一种用于铁路信号系统全线统一接地的电缆，它可以使大范围的铁路电气系统各个工作点接地点为基本保持一致，使系统设备接地安全可靠，消除了由于不同设备之间的电位差引起的电位不平衡电流，实现了对人员和设备的有效可靠防护。目前使用的综合贯通地线包括缆芯和包覆在所述缆芯外部的外护套，其缆芯包括按一定绞合方式绞合的至少一根报警绝缘线和多根铜线。由于铁路沿线所有设备均与同一条贯通地线连接，可保证全线所有信号传输设备的接地电位在任意时刻都保持一定的平衡。现在铁路所使用的铁路综合贯通地线是铅包铜线，即在铜绞线外包覆一层铅套，利用铅的导电性能和...
【技术保护点】
１．一种导电高分子护套材料的制备方法，其特征在于导电高分子护套材料的组份按质量百分比为热塑性高分子树脂为６０－３０％，纳米级导电炭黑为２５－３０％，导电碳纤维或导电剂为５－１４％，增韧剂为１０－１８％，加工助剂为０．５－１．５％和分散剂为１－３％的混合物，先将各组份原料按所需的质量百分比进行混合、搅拌均匀后，经特殊螺杆组合的双螺杆挤出机熔融、挤出、冷却、切粒、干燥和包装形成产品材料；或将热塑性高分子树脂、导电炭黑、导电碳纤维、增韧剂、抗氧老化剂、分散剂构成的混合物加入到密炼机中进行充分捏合、混炼、分散后，再用双辊开炼机混炼压延成片，粉碎机破碎，然后将破碎料经单螺杆挤出机熔融...
【技术特征摘要】
【专利技术属性】
技术研发人员：宋钦兰，王林茂，丁玉梅，
申请(专利权)人：青岛威东科高分子材料有限公司，
类型：发明
国别省市：95