The invention discloses a composite nano material graphene and MoS2 and its preparation method, composite material consisting of graphene and MoS2 nano composite materials, between graphene and MoS2 nano material mass ratio of 1: 1-4: 1; the preparation method is to use the chemical oxidation of graphite prepared graphite oxide nanosheets, and molybdate dissolved in deionized water to form a solution of 0.02 ~ 0.07M, adding L- cysteine as sulfur source and reducing agent, L- cysteine and molybdate mass ratio of 5: 1 to 12: 1, then the graphite oxide nanosheets into the solution, ultrasonic treatment of graphite oxide nanosheets fully dispersed in hydrothermal reaction solution, the mixture into a sealing hydrothermal reactor, through a one-step hydrothermal synthesis method of composite nano material graphene and MoS2 composite materials, graphene nano The mass ratio of the film to molybdenum disulfide is 1: 1-4: 1. The method of the invention has the advantages of mild reaction condition and simple process. The nano composite material of the invention is the synthesis of graphene and MoS2 as a new energy battery electrode materials, high performance lubricant state and the catalyst carrier has wide application.
【技术实现步骤摘要】
本专利技术涉及复合纳米材料及其制备，尤其涉及石墨烯与MO&的复合纳米材料及其 制备方法，属于无机复合纳米材料、新能源材料及其制备领域。
技术介绍
石墨烯纳米片以其独特的二维纳米片结构具有众多独特的物理、化学和力学等性 能，具有重要的科学研究意义和广泛的应用前景。石墨烯材料的发现者获得2010年诺贝尔 奖更是激发了人们对石墨烯材料研究的极大兴趣。石墨烯纳米片具有极高的比表面积、高 的导电和导热性能、超强的力学性能。最近人们对石墨烯纳米片作为微纳米电子器件、新能 源电池的电极材料、固体润滑剂和新型的催化剂载体的应用进行了广泛地研究。另一方面，MO&具有类似石墨的典型层状结构。MO&层状结构为三明治的层状 结构，其层内是很强的共价键(S-Mo-S)，层间则是较弱的范德华力，层与层之间容易剥离。 MoS2具有良好的各向异性与较低的摩擦因数，MoS2能很好地附着在金属表面发挥润滑功 能，特别是在高温、高真空等条件下仍具有较低的摩擦系数，是一种优良的固体润滑剂。 MoS2也是一种良好的催化脱硫的催化剂载体。另外具有层状结构的MO&作为主体材料...
【技术保护点】
１．一种石墨烯与ＭｏＳ２的复合纳米材料，其特征在于复合材料由石墨烯和ＭｏＳ２纳米材料复合构成，石墨烯与ＭｏＳ２纳米材料的之间物质量之比为１∶１－４∶１。
【技术特征摘要】
【专利技术属性】
技术研发人员：陈卫祥，陈涛，常焜，李辉，马琳，
申请(专利权)人：浙江大学，
类型：发明
国别省市：86