The invention provides a preparation method of polyether silicone oil, which comprises a reaction bottle, raw material, catalyst, in the four mouth flask, the first reaction material (low hydrogen containing silicone oil, allyl polyoxyalkylene ether) with 25% mass fraction of toluene azeotropic dehydration, and then to the PT mass fraction is 30 * 10 6 the chloroplatinic acid isopropyl alcohol solution as catalyst, heating in nitrogen atmosphere at 100 DEG C, the reaction of 4 ~ 4.5H, the solvent is evaporated, to polyether modified polysiloxane, prepared using a simple process, high and low temperature resistance, aging resistance, lubrication, soft, good spreadability and emulsion stability excellent the properties of polyether modified polysiloxane.
【技术实现步骤摘要】
本专利技术涉及一种化工原料的制备方法，尤其是一种聚醚硅油的制备方法。
技术介绍
目前，聚醚改性聚硅氧烷的制备，是以高含氢硅油为原料，采用调聚法制成低含氢 硅油，同时，以丙烯醇为起始剂、NaOH为催化剂，进行环氧乙烷、环氧丙烷的开环共聚，制成 端烯丙基聚氧烯醚；再用端烯丙基聚氧烯醚对低含氢硅油进行接枝改性，但聚硅氧烷乳化 比较困难。
技术实现思路
本专利技术针对现有技术的缺陷，提供一种实用性的聚醚硅油的制备方法。 为了实现上述目的，本专利技术采取以下措施来实现 —种聚醚硅油的制备方法，包括反应瓶，原料，催化剂，其特征在于在四口烧瓶中， 先将反应原料(低含氢硅油、端烯丙基聚氧烯醚)与质量分数为25%的甲苯共沸脱水，然后 以铂质量分数为30X10-6的氯铂酸异丙醇溶液作为催化剂，于氮气氛下加热至IO(TC，反 应4 4. 5h，蒸去溶剂后，得聚醚改性聚硅氧烷的方法。 本专利技术相对于已有技术具有如下特点本专利技术采用简单的工艺，制得耐高低温、抗 老化、润滑、柔软、良好的铺展性和乳化稳定性等优异性能的聚醚改性聚硅氧烷。具体实施例方式将111. 5g 二甲基环硅氧烷混合物、6. 5g高含氢硅油和2. 2g六甲基二硅氧烷加入 反应釜中，以浓硫酸作催化剂，在60 65t:下反应3 5h ;然后降至室温，用碳酸氢钠中 和，抽滤，11(TC下真空蒸馏脱去低沸物，得活性氢质量分数为0.09^的低含氢硅油。然后 在高压反应釜中，加入一定量的丙烯醇和碱催化剂，压紧釜盖，用N2置换3次；抽空升温，在 90 11(TC下边搅拌边加入环氧乙烷、环氧丙烷；加料完毕，熟化反应至釜内压力为...
【技术保护点】
一种聚醚硅油的制备方法，包括反应瓶，原料，催化剂，其特征在于在四口烧瓶中，先将反应原料（低含氢硅油、端烯丙基聚氧烯醚）与质量分数为２５％的甲苯共沸脱水，然后以铂质量分数为３０×１０↑［－６］的氯铂酸异丙醇溶液作为催化剂，于氮气氛下加热至１００℃，反应４～４．５ｈ，蒸去溶剂后，得聚醚改性聚硅氧烷的方法。
【技术特征摘要】
【专利技术属性】
技术研发人员：谢瑜，金珠，韩璐，
申请(专利权)人：吴江市方霞企业信息咨询有限公司，
类型：发明
国别省市：32[中国|江苏]