一种硅烷化的分子筛罗丹明B吸附剂及其制备方法技术

一种硅烷化的分子筛功能化罗丹明B吸附剂，其结构式为：其制备方法是通过氨水引发，以N，N-二甲基甲酰胺为溶剂室温下搅拌24小时，在SBA-15内腔表面引入硅烷偶联剂3-(甲基丙烯酰氧)丙基三甲氧基硅烷，然后依次用N，N-二甲基甲酰胺，丙酮，甲醇，去离子水洗涤抽滤，100℃真空干燥过夜，即得罗丹明B吸附材料。本发明专利技术所涉及的制备过程简单，采用氨水引发合成方法，节省了反应时间，节约了有机溶剂；所制得的分离材料结构新颖，应用灵活，可以用于吸附罗丹明B。

Silane molecular sieve rhodamine B adsorbent and preparation method thereof

The function of rhodamine B adsorbent a silanized molecular sieve, the structural formula: the preparation method is by ammonia caused by N, N-, two methyl formamide as solvent and stirred at room temperature for 24 hours, the introduction of silane coupling agent 3- on the inner surface of SBA-15 (Methacryloyloxy) Bing Jisan dimethoxysilane then, followed by N, N- two methyl formamide, methanol, acetone, deionized water washing filtration, vacuum drying at 100 overnight, namely rhodamine B adsorption material. The preparation process of the invention relates to a simple, using ammonia caused synthesis method, saves the reaction time, saves organic solvent; the separation material structure is novel, flexible application, can be used for the adsorption of Luo Danming B.

【技术实现步骤摘要】

本专利技术涉及一种分子筛材料及其制备方法，尤其涉及一种新型硅烷化分子筛罗丹明B吸附材料，并且是一种能够在降解过程不使生物大分子失活的新型降解材料的制备方法。
技术介绍
近年来，随着现代化工业的发展，有机废水对环境的影响越来越严重，但传统的有机污水处理方法往往能耗大、降解不完全，甚至有时造成二次污染。新型罗丹明B吸附材料作为一种新型的同时具有吸附和生物降解功能的吸附剂，已经被证明是一种适用于工业废水以及生物废弃物中罗丹明B有效处理的功能性材料，迅速成为分析化学和生物化学领域的重要研究对象，受到国内外学者的密切关注。新型罗丹明B吸附材料作为一种新型的同时具有吸附和生物降解功能的吸附剂， 已经被证明是一种适用于工业废水以及生物废弃物中罗丹明B有效处理的功能性材料，得到越来越广泛的重视和应用，相关的研究也在急剧增长。
技术实现思路
鉴于上述，本专利技术的目的旨在公开一种硅烷化的分子筛罗丹明B吸附剂。该吸附剂是一种新型的分离材料，这种材料结构新颖，应用灵活，可以用于罗丹明B的特异性吸附和降解罗丹明B与生物大分子结合复合物，而达到不使生物大分子失活的应用效果。本专利技术的另一目的在于提供一种硅烷化本文档来自技高网...