一种以草本植物为原料制备植物纤维素膜的方法技术

本发明专利技术公开了一种以草本植物为原料制备植物纤维素膜的方法，包括步骤：(1)以草本植物为原料，经提取，得到植物纤维素；(2)将上述植物纤维素、抗氧化剂和溶剂N-甲基吗啉-N-氧化物水溶液混合均匀，制得植物纤维素溶液；(3)将上述植物纤维素溶液经喷膜或刮制成膜，经后处理得到植物纤维素膜。该方法工艺简单，绿色无污染，制得的植物纤维素膜具有良好的机械性能和生物可降解性。

Method for preparing plant cellulose membrane by using herbaceous plant as raw material

The invention discloses a method for preparing cellulose membrane, using plant as raw materials, which comprises the following steps: (1) with herbaceous plants as raw material, after extraction, obtained plant cellulose; (2) mixing the plant cellulose, antioxidant and solvent N- -N- methyl morpholine oxide aqueous solution uniformly prepared cellulose solution; (3) the plant cellulose solution by spraying film or film made by scraping and postprocessing of plant cellulose film. The process is simple, green and pollution-free. The prepared cellulose membrane has good mechanical and biodegradability.

【技术实现步骤摘要】

本专利技术涉及纤维素膜的制备领域，具体涉及一种以草本植物为原料制备植物纤维 素膜的方法。
技术介绍
植物纤维素是地球上最丰富的可再生有机资源，我国仅稻草、麦草、蔗渣、芦苇、竹 子等非木材纤维年产量就超过10亿吨，是取之不尽的天然高分子化工原料和能源。植物纤 维素材料无毒，而且抗水性强，因此可以以粉状、片状、膜以及长短丝等不同形式出现。如能 充分利用自然界中的植物纤维素，不仅有利于保护环境，而且可以缓解目前由于日益减少 的油气资源所带来的能源压力。纤维素的分子间及分子内具有极强的氢键作用，使得纤维素难以被常规溶剂所直 接溶解，传统的纤维素膜的制备方法是粘胶法和铜氨法，产品分别为玻璃纸和铜络玢，而且 已有广泛的应用。但是粘胶法过程中会放出和等有毒物质，严重污染环境；铜氨法 中铜和氨回收困难，加之污染严重，使传统方法的进一步发展均受到了严重的制约。近年来，人们致力于研究适用于纤维素溶解的新型溶剂体系，并且取得了一定 的成果，例如NH3/NH4SCN体系、LiCl/DMAc(即二甲基乙酰胺)体系、ΝΜΜ0(即N-甲基吗 啉-N-氧化物)/H20体系等。目前，ΝΜΜ0/Η20体系是最被重视的本文档来自技高网...

【技术保护点】
１．一种以草本植物为原料制备植物纤维素膜的方法，包括步骤：（１）以草本植物为原料，经提取，得到植物纤维素；（２）将步骤（１）中的植物纤维素、抗氧化剂和水的质量百分含量为１０％－１５％的Ｎ－甲基吗啉－Ｎ－氧化物水溶液混合均匀，制得植物纤维素溶液；（３）将步骤（２）中的植物纤维素溶液制成膜，经后处理得到植物纤维素膜。

【技术特征摘要】

【专利技术属性】
技术研发人员：李文江，代琛，谢飞，
申请(专利权)人：李文江，
类型：发明
国别省市：86