The invention discloses a preform weaving process of carbon carbon crucible for monocrystalline silicon furnace. The steps are as follows: S1. Calculate the total winding layers according to the design size and density requirements of the preform, so as to calculate the total length of weft free cloth, mesh tire and fiber filament, and carry out continuous winding; S2. Lay a layer of plain cloth on the tooling, then a layer of mesh tire, and then use fiber in both horizontal and vertical directions The core of the uniform winding is the horizontal and vertical filament winding at the same time. The invention adopts the preform weaving process of the carbon carbon crucible for the monocrystalline silicon furnace, greatly improving the strength of the crucible, thereby improving the service life of the crucible, and reducing the raw material cost and the processing cost.
【技术实现步骤摘要】
一种单晶硅炉用碳碳坩埚预制体编织工艺
本专利技术涉及碳碳坩埚制备工艺
,特别是涉及一种单晶硅炉用碳碳坩埚预制体编织工艺。
技术介绍
预制体是制作碳碳复合材料坯体,直接影响碳碳产品使用寿命。现在碳碳复合材料广泛应用于光伏行业中单晶硅拉制环节,随着光伏平价上网的需求,各环节成本需进一步降低。现有的坩埚预制体的编制方式为在工装上先铺设一层平纹布,切断后铺设网胎,针刺后再铺设一层斜纹布,再切断铺设网胎,依次反复铺设、针刺。这种编织工艺会在每层炭布的首尾处出现接茬现象,导致碳碳坩埚在拉制单晶硅时受到外力挤压后因接茬处强度低而破坏,缩短了产品的使用寿命。
技术实现思路
本专利技术的目的是提供一种单晶硅炉用碳碳坩埚预制体编织工艺,大大提高坩埚的强度,从而提高坩埚的使用寿命,同时降低原料成本和加工成本。为实现上述目的,本专利技术提供了一种单晶硅炉用碳碳坩埚预制体编织工艺,步骤如下:S1、根据预制体设计尺寸、密度要求计算总缠绕层数,从而计算出所需无纬布、网胎、纤维长丝总长度,进行连续式缠绕;S2、在工装上先铺一层平纹布,之后铺一层网胎,然后在横向、纵向均用纤维长丝均匀缠绕,再针刺,如此反复至预制体制作完成,其核心为横向、纵向长丝同时均匀缠绕。优选的,步骤S2中,预制体的设置方式为自下而上依次设有平纹布、网胎、缠绕层和网胎,缠绕层为横向、纵向纤维长丝缠绕结构。优选的,步骤S2中,针刺密度为18针/cm3。因此,本专利技术采用上述一种单晶硅炉用碳碳坩埚预制体编织工艺 ...
【技术保护点】
1.一种单晶硅炉用碳碳坩埚预制体编织工艺,其特征在于,步骤如下:/nS1、根据预制体设计尺寸、密度要求计算总缠绕层数,从而计算出所需无纬布、网胎、纤维长丝总长度,进行连续式缠绕;/nS2、在工装上先铺一层平纹布,之后铺一层网胎,然后在横向、纵向均用纤维长丝均匀缠绕,再针刺,如此反复至预制体制作完成,其核心为横向、纵向长丝同时均匀缠绕。/n
【技术特征摘要】
1.一种单晶硅炉用碳碳坩埚预制体编织工艺,其特征在于,步骤如下:
S1、根据预制体设计尺寸、密度要求计算总缠绕层数,从而计算出所需无纬布、网胎、纤维长丝总长度,进行连续式缠绕;
S2、在工装上先铺一层平纹布,之后铺一层网胎,然后在横向、纵向均用纤维长丝均匀缠绕,再针刺,如此反复至预制体制作完成,其核心为横向、纵向长丝同时均匀缠绕。...
【专利技术属性】
技术研发人员:王金铎,啜艳明,郭宾,周倩,胡士伟,
申请(专利权)人:保定顺天新材料股份有限公司,
类型:发明
国别省市:河北;13