The invention discloses a synthesis method of lithium sulfide powder, which comprises the following steps: (1) under the protection of inert atmosphere, uniformly mix silicon sulfide and lithium oxide, transfer them to the reactor and seal them; (2) heat the mixture in the reactor for a certain period of time; (3) when the reaction is finished, reduce it to room temperature, take out the solid products from the reactor, and recover them by solvent method The amount of silicon sulfide; (4) the residual solid products were separated by solvent method to get lithium sulfide powder. The synthesis method of lithium sulfide powder has the advantages of simple process, low cost and easy industrialization.
【技术实现步骤摘要】
一种硫化锂粉体的合成方法
本专利技术属于材料合成
，具体涉及一种硫化锂粉体的合成方法。
技术介绍
硫化锂是一种无机化合物，其化学式为Li2S，属于立方晶系，反萤石型结构，在空气中极易潮解。目前，有关硫化锂的合成方法较少，中国专利技术专利(公开号CN106784754A)公开了将硫粉放入含有三乙基硼氢化锂的四氢呋喃溶液中，待充分反应后，将固体粉末与液体分离即得到硫化锂；中国专利技术专利(公开号CN108190845A)公开了将硫粉与金属锂粉加入液氨中，经充分反应后，将固体粉末与液体分离即得到硫化锂。上述两类方法都需要用到有毒有害的溶剂，效率较低，成本较高，价格昂贵，难以实现工业化生产。此外，采用硫酸锂和焦炭为原料，通过800-900℃高温锻烧法亦可获得硫化锂。但该方法制得的硫化锂存在纯度不高，批次性差，耗能等缺点，也不易于工业化生产。因而，发展一种新型、高效、环境友好的硫化锂合成方法具有重要意义。
技术实现思路
本专利技术目的是为了解决现有技术的不足，提供一种高效、低成本、环境友好、易于工业化生产的合...
【技术保护点】
1.一种硫化锂粉体的合成方法，其特征在于，包括如下步骤：/n(1)在惰性气氛保护下，将硫化硅与氧化锂均匀混合，转移至反应器并密封；/n(2)将反应器内的混合物加热至一定温度并保温反应一定时间；/n(3)反应结束后降至室温，取出反应器中的产物，溶剂法回收过量硫化硅；/n(4)溶剂法分离剩余固体产物即可得到硫化锂粉体。/n
【技术特征摘要】
1.一种硫化锂粉体的合成方法，其特征在于，包括如下步骤：
(1)在惰性气氛保护下，将硫化硅与氧化锂均匀混合，转移至反应器并密封；
(2)将反应器内的混合物加热至一定温度并保温反应一定时间；
(3)反应结束后降至室温，取出反应器中的产物，溶剂法回收过量硫化硅；
(4)溶剂法分离剩余固体产物即可得到硫化锂粉体。
2.如权利要求1所所述一种硫化锂粉体的合成方法，其特征在于，所述硫化硅和氧化锂的纯度均不低于90％。
3.如权利要求1所述一种硫化锂粉体的合成方法，其特征在于，所述步骤(1)中硫化硅与氧化锂的摩尔比为(1-3)：2。
4.如权利要求1所述一种硫化锂粉体的合成方法，其特征在于，所述步骤(2)中，加热的升温速率为0.5-20℃/min，保温反应温度为100-...
【专利技术属性】
技术研发人员：梁初，王俊豪，孙鑫，张俊，黄辉，张文魁，甘永平，夏阳，
申请(专利权)人：浙江工业大学，
类型：发明
国别省市：浙江;33