The invention relates to a solvent for polyethylene catalyst, which is a mixture of propane and C4-C6 alkanes with a mass ratio of (1 3): (1 3). Compared with the existing technology, the new solvent is prepared by mixing propane with propane with specific technical requirement and C4-C6 alkanes with specific technical requirement as main components. The new solvent has the characteristics of low viscosity, good fluidity and uniform dispersion. It also shows excellent inertia for the catalytic reaction of polyolefin and has no harmful effect on the normal production and final product of polyolefin. The solvent also has the characteristics of low boiling point and volatility, which makes it easy to desorb from the polyolefin resin produced by the reaction.
【技术实现步骤摘要】
一种聚乙烯催化剂用溶剂
本专利技术涉及催化剂用的溶剂，具体涉及混合烷烃类聚乙烯聚乙烯催化剂用的特制溶剂。
技术介绍
在聚烯烃行业中应用的催化剂预聚合或催化剂配制所用溶剂要求低粘度、易挥发，化学性质稳定、脱附容易、无毒害等工艺条件。目前聚烯烃行业常用的由单一组成的如为碳原子数4到10的直链或支链烷烃如己烷，或是碳原子数4到10的环烷烃或芳烃，均很难同时满足上述要求。此外，常用的为碳原子数4到10的直链或支链烷烃如己烷，或是碳原子数4到10的环烷烃或芳烃，通常不易脱附或有芳香烃类杂质，均对生产过程及最终产品的品质有不良影响，且不利于健康和环保。CN1041162中用单一烷烃丙烷在催化剂预聚合过程中，由于其挥发性过强，闪点较低，操作的安全性下降。CN1330087中用己烷以上的脂肪链烷烃及环烷烃，如庚烷、辛烷、癸烷、煤油等作为溶剂，但在聚乙烯生产及催化剂配制脱除工序中较难挥发、难脱除。CN105085750中采用C5-C6的直链烷烃及其异构体作为聚丙烯催化剂预聚合溶剂，在聚乙烯生产过程中脱出不够彻底，容易在聚乙烯产品中产生异味。
技术实现思路
本专利技术的目的就是为了克服上...
【技术保护点】
1.一种聚乙烯催化剂用溶剂，其特征在于，为质量比为(1‑3)：(1‑3)丙烷和C4～C6烷烃的混合物。
【技术特征摘要】
1.一种聚乙烯催化剂用溶剂，其特征在于，为质量比为(1-3)：(1-3)丙烷和C4～C6烷烃的混合物。2.根据权利要求1所述的聚乙烯催化剂用溶剂，其特征在于，所述的溶剂在15.6℃温度测试条件下的比重为0.58～0.62。3.根据权利要求1所述的聚乙烯催化剂用溶剂，其特征在于，所述的溶剂的酸度以重量计的浓度<2ppm；溶剂中含其它碳氢化合物重量百分浓度<5％，不饱和烃以重量计的浓度<500ppm，水以重量计的浓度<20ppm，硫以重量计的浓度<5ppm，色度<15，不挥发物<0.001g/100ml，过氧化物以重量计的浓度<0.1ppm，苯类以重量计的浓度<0.1ppm。4.根据权利要求1所述的聚乙烯催化剂用溶剂，其特征在于，所述的丙烷在15.6℃温度测试条件下的比重为0.50～0.52。5.根据权利要求1或4所述的聚乙烯催化剂用溶剂，其特征在于，所述的丙烷的重量百分比浓度为95％。6.根据权利要求1或4所述的聚乙烯催化剂用溶剂，其特征在于，所述的丙烷的酸度以重量计的浓度<2ppm；丙烷中...
【专利技术属性】
技术研发人员：陈玉龙，
申请(专利权)人：上海立得催化剂有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。