The invention discloses an unsaturated polyester spraying white primer and its preparation process, which relates to the technical field of paint production, and solves the problem of poor overall adhesion caused by poor stability of the paint, thereby leading to paint stripping easily in the use process. It consists of 5-9 parts of maleic anhydride, 9-15 parts of isophthalic anhydride, 10-18 parts of propylene glycol, 3-5 parts of adhesion promoter, 2-3 parts of polyoxyethylene trisiloxane, 3-6 parts of alkyl gluconamide, 5-8 parts of butyl acetate, 6-7 parts of xylene, 4-7 parts of dispersant and 2-3 parts of anti-sedimentation agent. The unsaturated polyester spraying white primer in the invention has good adhesion and stability, and is not easy to depaint in the use process.
【技术实现步骤摘要】
一种不饱和聚酯淋涂白底漆及其制备工艺
本专利技术涉及油漆生产
，更具体地说，它涉及一种不饱和聚酯淋涂白底漆及其制备工艺。
技术介绍
油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。在公告号为CN106916472A的中国专利技术专利中公开了一种耐磨木器用油漆及其制备工艺，其由以下重量份的原料组成：由以下重量份的原料组成：硅灰石10～15份、蒙脱土5～15份、高岭土5～10份、滑石粉5～10份、松香树脂5～10份、聚氨酯1～5份、丙烯酸树脂1～5份、助剂5～10份和水适量；所述助剂由以下重量份的原料组成：茶油10～15份、碳酸钙5～15份、豆粕5～15份、丙酮1～5份、醋酸丁酯1～5份、乳化剂1～3份、防潮剂1～3份、流平剂1～3份和水适量。上述专利中，蒙脱土和高岭土具有很好的分散性及粘黏度，可以提高漆料的吸附性，但蒙脱土由于层间的大量无机离子而表现出来的疏油性，不利于其在聚合物基体中的分散，且高岭土具有强的耐酸性能，但其耐碱性能差，导致耐磨木器用油漆在使用过程中，其整体的稳定性较差，且容易发生脱漆的现象，因此，需要提出一种新...
【技术保护点】
1.一种不饱和聚酯淋涂白底漆，其特征在于，包括如下重量份数的组分：顺丁烯二酸酐 5～9份；间苯二甲酸酐 9～15份；丙二醇 10～18份；附着力促进剂 3～5份；聚氧乙烯三硅氧烷 2～3份；烷基葡糖酰胺 3～6份；醋酸丁酯 5～8份；二甲苯 6～7份；分散剂 4～7份；防沉剂 2～3份。
【技术特征摘要】
1.一种不饱和聚酯淋涂白底漆，其特征在于，包括如下重量份数的组分：顺丁烯二酸酐5～9份；间苯二甲酸酐9～15份；丙二醇10～18份；附着力促进剂3～5份；聚氧乙烯三硅氧烷2～3份；烷基葡糖酰胺3～6份；醋酸丁酯5～8份；二甲苯6～7份；分散剂4～7份；防沉剂2～3份。2.根据权利要求1所述的不饱和聚酯淋涂白底漆，其特征在于，所述不饱和聚酯淋涂白底漆中还加入重量份数为3～5份的硅溶胶。3.根据权利要求2所述的不饱和聚酯淋涂白底漆，其特征在于，所述不饱和聚酯淋涂白底漆中还加入重量份数为1.2～2.1份的十二烷基苯磺酸钠。4.根据权利要求1所述的不饱和聚酯淋涂白底漆，其特征在于，所述不饱和聚酯淋涂白底漆中还加入重量份数为2.5～5份的灰云铁。5.根据权利要求1所述的不饱和聚酯淋涂白底漆，其特征在于，所述附着力促进剂选用环氧磷酸酯、胺基硅烷、聚氨酯改性磷酸酯化合物或多官能磷酸酯丙烯酸酯低聚物。6.根据权利要求1所述的不饱和聚酯淋涂白底漆，其特征在于，所述分散剂选用聚乙二醇、油氨基油酸酯或聚丙烯酰...
【专利技术属性】
技术研发人员：梁文文，
申请(专利权)人：上海立邦长润发涂料有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。