The invention discloses a preparation method of ceramics, and the preparation method is simple and feasible. The preparation method of the invention comprises: (a) mixing alumina powder, camphene and fatty acid polycondensate to obtain slurry; (b) forming green body by grouting; (c) drying green body, and then heat treating to obtain gradient porous alumina ceramics. The gradient porous alumina ceramics have the characteristics of directional pore distribution, controllable shape, network-connected pore and high porosity by using the properties of different crystallization rates of camphene at different temperatures. The problems of poor pore distribution, difficult pore shape control and low porosity of the gradient porous ceramics obtained by the existing preparation methods are solved.
【技术实现步骤摘要】
一种陶瓷的制备方法
本专利技术涉及一种陶瓷的制备方法。
技术介绍
陶瓷种类繁多，根据成孔方法和孔隙结构其大致又可分为多孔陶瓷、蜂窝陶瓷、泡沫陶瓷、波纹陶瓷以及孔梯度陶瓷和多孔功能陶瓷等种类。多孔陶瓷与其它多孔材料相比具有化学稳定性好、机械强度良好、刚度好、耐热性好、热膨胀系数低、密度低、孔隙率高等优点，因而多孔陶瓷在高温隔热、主动冷却、燃料电池、过滤器、吸音等领域获得广泛的应用。梯度多孔陶瓷的特点是具有大量气孔，且孔径随材料尺寸作梯度分布的陶瓷，气孔的形状、含量、孔径及其分布对其性能和功能有着重大影响，因此其制备工艺除具有一般陶瓷工艺的特点外，还应具有如何形成比较合理的孔结构的工艺机制。目前孔梯度陶瓷材料主要采用注浆成型和溶胶凝胶法，但是该方法成型制备孔梯度陶瓷时，各层是分别注浆而成，由于不同粒度层的干燥和烧结收缩率不同，在制品的成型过程中常常出现分层或分离现象，造成孔分布性差，陶瓷成品性能下降。
技术实现思路
为解决上述问题，本专利技术采用技术方案为：一种陶瓷的制备方法，包括以下步骤：一、将氧化铝粉末、莰烯(C10H16)和脂肪酸缩聚物混合后放入恒温球磨机中，在50...
【技术保护点】
1.一种陶瓷的制备方法，其特征在于，包括以下步骤：（a）将氧化铝粉末、莰烯和脂肪酸缩聚物混合后放入恒温球磨机中，在50～60℃下球磨湿混20～30h得混合浆料，其中氧化铝粉末与莰烯的体积比为1∶4～19，脂肪酸缩聚物的质量是氧化铝粉末和莰烯总质量的1％～3％，所述脂肪酸缩聚物为Texaphor963；（b）将模具浸入液氮中1～3min后将步骤一得到的浆料倒入模具中，再静置30～60min，然后脱模得坯体，其中以模具底面为基准，液氮液面位于模具底部的1/2～2/3处；(c)将坯体置于室温、空气气氛条件下放置64～80h后，再在30～50℃温度下干燥64～80h；(d)将经上述...
【技术特征摘要】
1.一种陶瓷的制备方法，其特征在于，包括以下步骤：（a）将氧化铝粉末、莰烯和脂肪酸缩聚物混合后放入恒温球磨机中，在50～60℃下球磨湿混20～30h得混合浆料，其中氧化铝粉末与莰烯的体积比为1∶4～19，脂肪酸缩聚物的质量是氧化铝粉末和莰烯总质量的1％～3％，所述脂肪酸缩聚物为Texaphor963；（b）将模具浸入液氮中1～3min后将步骤一得到的浆料倒入模具中，再静置30～60min，然后脱模得坯体，其中以模具底面为基准，液氮液面位于模具...