The invention discloses a low-cost mineral admixture, which is prepared from the following raw materials: 25 weight parts of limestone powder, 60 weight parts of natural sand, 5 weight parts of cement clinker, 15 weight parts of silica fume, 12 weight parts of kaolin powder, 15 weight parts of fly ash, 2 weight parts of calcium sulfate, 15 weight parts of blast furnace waste slag powder and waste electrolytic aluminium cell slag powder. The invention can effectively improve the compressive strength and early strength of concrete, make full use of industrial waste residue, reduce the usage of active components such as cement clinker, greatly reduce the production cost, and have good compatibility with the admixtures used.
【技术实现步骤摘要】
低成本矿物掺合料
本专利技术涉及建筑材料
，具体涉及一种低成本矿物掺合料。
技术介绍
掺合料通常具有降低混凝土成本、改善混凝土工作性能、提高混凝土物理性能的特点，目前应用的掺合料以矿粉、粉煤灰为主，具有需水量大、成本高、混凝土早期强度发展缓慢的缺点。国内外混凝土掺合料往往因过于单一导致胶凝材料活性差，混凝土强度较低，或成本过高大大影响了工业废料的使用。
技术实现思路
本专利技术的目的是提供一种具有成本低廉、改善混凝土和易性，提高混凝土强度的低成本矿物掺合料。为了实现本专利技术目的，采用以下技术方案：一种低成本矿物掺合料，由以下原料制备而成：石灰石粉25重量份；天然砂60重量份，水泥熟料5重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份，高炉废渣粉15重量份，废电解铝槽渣粉。本专利技术有益效果：本专利技术能有效提高混凝土的抗压强度和早期强度，同时充分利用了工业废渣，降低了水泥熟料等活性组份的使用量，大大降低了生产成本，并且对使用的外加剂相容性好。具体实施方式实施例1一种低成本矿物掺合料，由以下原料制备而成：石灰石粉25重量份；天然砂60重量份，水泥熟料5重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份，高炉废渣粉15重量份，废电解铝槽渣粉。以上所述仅为本专利技术的优选实施例而已，并不用于限制本专利技术，对于本领域的技术人员来说，在本专利技术的精神和原则内可以有各种更改和变化，这些等同的变型或替换等，均包含在本专利技术的保护范围之内。
【技术保护点】
1.一种低成本矿物掺合料，其特征在于，石灰石粉25重量份；天然砂60重量份，水泥熟料5重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份，高炉废渣粉15重量份，废电解铝槽渣粉。
【技术特征摘要】
1.一种低成本矿物掺合料，其特征在于，石灰石粉25重量份；天然砂60重量份，水泥熟料5重量份，硅灰1...
【专利技术属性】
技术研发人员：陆远林，
申请(专利权)人：扬州佳奕金属材料有限公司，
类型：发明
国别省市：江苏,32