氧化铈纳米介孔球的制备方法技术
Preparation of cerium oxide nano mesoporous ball
The invention relates to a preparation method of cerium oxide nano mesoporous spheres. The method of the invention is to dissolve cerium salt in 5 ~ 50us/cm deionized water and obtain a homogeneous mixed solution with a mass percentage of 1% and 10%, sealed in a high-pressure reactor and reacting for 24h to 72h at 180 ~ 200 temperature. After natural cooling, it is filtered and washed to neutralize and dry the mesoporous cerium oxide ball powder. Body. The invention can promote the formation of two cerium oxide balls by controlling the thermodynamic and kinetic conditions of cerium oxide at low temperature conditions, by controlling the thermodynamic and kinetic conditions of cerium oxide. The size of the spherical cerium oxide particles is 50 80nm, which can be widely used in UV shielding, chemical mechanical polishing and catalyst. The preparation process is fast, simple, low cost, and can be produced in batches.
【技术实现步骤摘要】
氧化铈纳米介孔球的制备方法
本专利技术涉及一种氧化铈纳米介孔球的制备方法。
技术介绍
我国是稀土资源大国，在稀土储量上占据着绝对优势，其中铈的储量占全球储量65%以上，目前全球90%以上的氧化铈原料由中国提供。氧化铈作为一种重要的稀土氧化物，可广泛应用于催化剂、化学机械抛光、防紫外线化妆品。球形介孔氧化铈具有丰富的孔结构，比表面积较高，是一种较好的催化、化学机械抛光、紫外屏蔽材料。尤其是CeO2作为抛光料被广泛地应用于精密玻璃抛光和二氧化硅介质层的化学机械抛光,表现出优秀的抛光能力。一般认为球形粒径分布均匀、颗粒较小、稳定性好的纯度高球形氧化铈磨料是理想的抛光磨料。一方面可以提高抛光液的分散性、减少团聚沉淀现象，另一方面与传统磨料不同球形氧化铈磨料颗粒，在抛光过程中具有较好的流动性，与基质产生滑动的研磨效果，能消除抛光过程中普通磨料不规则的棱角对工件表面的划伤，防止抛光过程中对基质造成表面划痕，并且由于抛光压力是均匀分布在磨粒表面，颗粒破碎减少，切削性、耐磨性和流动性大幅提高，因而可以得到最佳抛光效果。目前，文献报道球形氧化铈制备中，中国专利CN102557102...
【技术保护点】
1.一种氧化铈纳米介孔球的制备方法，其特征在于该方法的具体步骤为：将铈盐溶于电导率为5～50us/cm去离子水中，得到质量百分比浓度为1%～10%的均匀的混合溶液，高压反应釜中密封，在180℃～200℃温度下反应24h～72h，自然冷却后，抽滤、洗涤至中性、干燥得到介氧化铈纳米介孔球粉体。
【技术特征摘要】
1.一种氧化铈纳米介孔球的制备方法，其特征在于该方法的具体步骤为：将铈盐溶于电导率为5～50us/cm去离子水中，得到质量百分比浓度为1%～10%的均匀的混合溶液，高压反应釜中密封，在180℃～200℃温度下反应24h～72h，自然冷却后，...
【专利技术属性】
技术研发人员：张登松，施利毅，颜婷婷，
申请(专利权)人：上海大学，安集微电子科技上海股份有限公司，
类型：发明
国别省市：上海,31