一种镧基钙钛矿的绿色合成方法技术
A green synthesis method of lanthanum perovskite
The present invention discloses a green synthesis method of lanthanum perovskite. First, plant water is extracted with water, and plant extract is prepared. Lanthanum nitrate and metal salt are added in the plant extract. After stirring and dissolving, drying, calcining at low temperature, that is, lanthanum perovskite is obtained. The synthesis method of the invention has rich raw material content, cheap and easy to get, easy to regenerate, simple process and convenient operation, and can get the perovskite type oxide of pure phase at low calcining temperature (500), which is beneficial to the industrialization of perovskite type oxide.
【技术实现步骤摘要】
一种镧基钙钛矿的绿色合成方法
本专利技术属于钙钛矿型氧化物的制备
，具体涉及一种镧基钙钛矿的绿色合成方法，以植物质为原料，在较低温度下煅烧，绿色合成镧基钙钛矿。
技术介绍
钙钛矿型氧化物(通式为：ABO3)是一类具有特殊结构和理化性质的复合氧化物，在催化、传感器、固体燃料电池等诸多领域有着广泛的应用和研究。尤其是在异相催化领域，钙钛矿型氧化物不仅具有“化学可裁剪性”，即：通过调控A位或者B位的元素组成，可调控其催化性能或者赋予其新的催化性能，而且廉价易得，有望成为替代铂族元素等贵金属催化剂的催化材料，具有良好的应用前景。研究表明，B位阳离子对钙钛矿型氧化物的电子结构具有重要的调控作用，进而影响钙钛矿型氧化物催化性能，而A位阳离子主要起到稳定结构的作用，对其催化活性的影响较小。镧基钙钛矿(LaMO3)在不同类型的催化中表现出良好的性能，是常被研究的钙钛矿型氧化物之一。与其它钙钛矿型氧化物的合成方法一致，LaMO3常见的合成方法有：高温固相法、共沉淀法、络合法、溶胶-凝胶法、燃烧法、冷冻干燥法、喷雾干燥法、反应球磨法、模板法等。这些传统的合成方法主要存在着两方面...
【技术保护点】
一种镧基钙钛矿的合成方法，其特征在于：包括：1)植物质用水提取，制备成浓度为5～120g/L的植物质提取液；2)在步骤1)得到的植物质提取液中加入硝酸镧及金属盐，其中硝酸镧与金属盐的摩尔比为1:0.8～1.2，硝酸镧与植物质提取液的配方比例为0.01～0.15g:1mL，待硝酸镧与金属盐充分溶解后，在65～95℃烘干20～50h，然后进行煅烧，煅烧时以2～12℃/min的升温速率从室温升至450～900℃后恒温2～7h，煅烧结束后得到镧基钙钛矿。
【技术特征摘要】
1.一种镧基钙钛矿的合成方法，其特征在于：包括：1)植物质用水提取，制备成浓度为5～120g/L的植物质提取液；2)在步骤1)得到的植物质提取液中加入硝酸镧及金属盐，其中硝酸镧与金属盐的摩尔比为1:0.8～1.2，硝酸镧与植物质提取液的配方比例为0.01～0.15g:1mL，待硝酸镧与金属盐充分溶解后，在65～95℃烘干20～50h，然后进行煅烧，煅烧时以2～12℃/min的升温速率从室温升至450～900℃后恒温2～7h，煅烧结束后得到镧基钙钛矿。2.根据权利要求1所述的镧基钙钛矿的合成方法，其特征在于：所述步骤1)中，制备植物质提取液的方法包括：将干净的植物质在50～80℃烘干，破碎得到植物质粉末；植物质粉末在25～35℃下用水提取，得到浓度为10～100g/L的植物质提取液。3.根据权利要求1所述的镧基钙钛矿的合成方法，其特征在于：所述步骤1)中，植物...
【专利技术属性】
技术研发人员：李清彪，王坤灿，黄俊杰，郝海姣，黄加乐，孙道华，
申请(专利权)人：厦门大学，
类型：发明
国别省市：福建,35