The present invention discloses a low alloy medium manganese wear-resistant steel hot rolled plate with a mass percentage of C0.6 to 0.8%, Si 0.1 ~ 0.2%, Mn 4.5 ~ 4.9%, P < 0.02%, S < 0.02%, Cr 3 3.5%, Cu0.4 1%, and the rest Fe and unavoidable impurities. The tensile strength of the hot rolled plate is not less than 700MPa, the yield strength is not less than 400Mpa, the impact toughness AKv at room temperature is more than 60J, the impact toughness at 20 C is AKv more than 30J, and the Brinell hardness of the surface is 180 240HB. Through the improvement of chemical composition optimization design and preparation method, the low alloy medium manganese wear-resistant steel has excellent wear resistance, corrosion resistance and mechanical properties, and has a strong potential for industrialization.
【技术实现步骤摘要】
低合金中锰耐磨钢热轧板及制备方法
本专利技术涉及耐磨热轧板
，特别是涉及一种低合金中锰耐磨钢热轧板及制备方法。
技术介绍
在疏浚、采矿、港口和电站等工程机械领域中，磨损是影响设备正常运行的主要原因之一，为国家和社会带来巨大的经济损失，耐磨材料及相关技术发展对我国节能节材和环境保护具有重要的意义。目前，在耐磨钢应用中以C、Mn、Cr等为主要合金元素，尤其是锰钢系列中先后开发出中、高锰多系列耐磨钢产品。高锰钢已经广泛应用于球磨机、破碎机等工程
，如Mn13钢在强烈冲击工况条件下，通过奥氏体向马氏体转变和加工硬化等作用机理，表面硬度大幅提高，进而耐磨性能得到优化。但是应用中发现高锰钢在冲击能量较小的工况条件下硬化系数较低，表面发生马氏体转变量较小，难以达到硬化和耐磨的效果，因此，适合中低冲击工况条件的中锰耐磨钢领域的研究热度正逐年增加。申请号2015107079409的专利“一种多元合金化高强高耐磨钢及热轧板的制造方法”公开了一种Mn含量8-10％的中锰耐磨钢热轧板工艺，主要通过Ti、V、Vb等微合金元素细化晶粒，形成合金碳化物等第二相粒子后弥散分布在晶粒内...
【技术保护点】
一种低合金中锰耐磨钢热轧板，其特征在于，成份质量百分比为：C 0.6～0.8％，Si 0.1～0.2％，Mn 4.5～4.9％，P≤0.02％，S≤0.02％，Cr 3.0‑3.5％，Cu 0.4‑1.0％，其余为Fe和不可避免的杂质。
【技术特征摘要】
1.一种低合金中锰耐磨钢热轧板，其特征在于，成份质量百分比为：C0.6～0.8％，Si0.1～0.2％，Mn4.5～4.9％，P≤0.02％，S≤0.02％，Cr3.0-3.5％，Cu0.4-1.0％，其余为Fe和不可避免的杂质。2.如权利要求1所述的耐磨钢热轧板，其特征在于，所述的C的质量百分比为0.65～0.75％；所述的Si的质量百分比为0.12～0.19％；所述的Mn的质量百分比为4.6～4.8％，所述的Cr的质量百分比为3.1-3.4％，所述的Cu的质量百分比为0.6-0.8％。3.如权利要求1所述的耐磨钢热轧板，其特征在于，所述的C的质量百分比为0.7％；所述的Si的质量百分比为0.14～0.16％；所述的Mn的质量百分比为4.7％，所述的Cr的质量百分比为3.2-3.3％；所述的Cu的质量百分比为...
【专利技术属性】
技术研发人员：王军祥，邢维宝，
申请(专利权)人：天津市宝月钢制品有限公司，
类型：发明
国别省市：天津,12